Corrosion Behavior of Slags with Different Basicities to Alumina Magnesia Castables

作     者：ZHANG Qiaoyan ZHU Boquan LI Xiangcheng 

作者机构：The Key State Laboratory Breeding Base of Refractories and Ceramics Wuhan University of Science and Technology 

出 版 物：《China's Refractories》 (中国耐火材料（英文版）)

年 卷 期：2012年第21卷第4期

页      面：17-21页

学科分类：0817[工学-化学工程与技术] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：basicity slag resistance alumina magnesia castables 

摘      要：Alumina magnesia castable crucible specimens were prepared using tabular corundum （ ≤ 5 mm ）, fused magnesia powder （ ≤0. 088 mm ） , fused spinel powder （ ≤0. 044 mm ） , and α-Al2O3. micropowder （d50 ≤0. 7 μm ） as main starting materials, batching, mixing, shaping, and drying. Slag resistance was determined by static crucible method at 1 600℃ for 3 h adopting two ladle slags with different basicities （3. 40 and 1.03 ）. The corrosion and penetration indexes and microstructure characteristics of the specimens after slag resistance test were analyzed to study the corrosion behaviors of the two slags to alumina magnesia castables. The results show that the corrosion of the low basicity slag to alumina magnesia custables is much more serious than that of the high basicity slag for that their reactions with castables form different products;for the low basicity slab,, the multi-phase coexistence of CA6 and compounds of CaO - Al2O3 -SiO2 in the materials together with volume expansion caused by the formation of CA6 intensify the slag corrosion and penetration ; for the high basicity slag, the reaction between slag and castables generates a CA2 dense layer and a large amount of in-situ MA in the interface, reducing the slag corrosion to the materials effectively.