Study on magnetic memory signals of medium carbon steel specimens with surface crack precut during loading process

作     者：DONG Lihong XU Binshi DONG Shiyun YE Minghui CHEN Qunzhi 

作者机构：Basic Department Ordnance Engineering College Shijiazhuang 050003 China National Key Laboratory for Remanufacturing of Armored Force Engineering Institute Beijing 100072 China National Key Laboratory for Remanufacturing of Armored Force Engineering Institute Beijing 100072 China National Key Laboratory for Remanufacturing of Armored Force Engineering Institute Beijing 100072 China Basic Department Ordnance Engineering College Shijiazhuang 050003 China Beijing Aeronautical Technology Research Center Beijing 100076 China 

出 版 物：《Rare Metals》 (稀有金属（英文版）)

年 卷 期：2006年第25卷第z1期

页      面：431-435页

核心收录：

学科分类：0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0703[理学-化学] 0702[理学-物理学] 

基　　金：This work was financially supported by the National Natural Science Foundation of China (No.50235030  50505052) 

主　　题：metal magnetic memory ferromagnetic materials surface crack precut Hp(y) zero value magnetic ordered state 

摘      要：Static tensile test and tensile-tensile fatigue test of medium carbon steel sheet specimens with surface crack precut were performed on MTS810 hydraulic testing machine to clear the meaning of the point of Hp(y) value zero. Magnetic memory signals were measured during the test process. The results show that only one point of Hp(y) zero value exists in all measured magnetic signal curves during the loading process, which should be a sign of intersection of positive-negative magnetic poles after magnetic ordered state appears and does not indicate the position of surface crack precut. The analysis shows that the surface crack precut can not interrupt the magnetic ordered state occurred during the test completely, hence its Hp(y) value is not zero. However, the crack extending to a penetrated defect at the instant of specimen′s fracture leads to the discontinuance of magnetic ordered state.