Fe-B-Y-Nb bulk metallic glasses in relation to clusters

作     者：CHENG Xu WANG Qing CHEN WeiRong DONG Chuang 

作者机构：State Key Laboratory of Materials ModificationDalian University of TechnologyDalian 116024China Department of Mechanical EngineeringDalian UniversityDalian 116622China 

出 版 物：《Science China(Physics,Mechanics & Astronomy)》 (中国科学：物理学、力学、天文学（英文版）)

年 卷 期：2008年第51卷第4期

页      面：421-426页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：the National Natural Science Foundation of China (Grant Nos. 50671018, 50631010 and 50401020) the National Basic Research Program of China (Grant No. 2007CB613902) 

主　　题：bulk metallic glass Fe-B-Y-Nb alloys cluster composition design 

摘      要：Bulk metallic glass formations in the Fe-B-Y-Nb quaternary alloy system were in-vestigated by using the cluster line rule in combination with the minor alloying principle. The Fe-B-Y ternary system was selected as the basic system and the intersections of cluster lines were taken as the basic ternary compositions. The basic compositions were further alloyed with minor amounts of Nb. After 3-5 at.% Nb was added,the basic composition Fe68.6B25.7Y5.7,which was developed from the most densely packed cluster Fe8B3,formed 3 mm bulk metallic glasses. These quaternary bulk metallic glasses (Fe68.6B25.7Y5.7)100-xNbx (x=3-5 at.%) are expressed approximately with a unified simple composition formula: (Fe8B3)1(Y,Nb)1. The (Fe68.6B25.7Y5.7)97Nb3 bulk metallic glass has the largest glass forming ability with the following characteristic parameters Tg=907 K,Tx=1006 K,Tg/Tl=0.644,γ=0.434,and longness t=22 mm. The combination of the cluster line rule and the minor-alloying principle is a promising new route towards the quantitative composition design of multi-component metallic glasses.