Dewetting Behavior of Hydrogen Bonded Polymer Complex Film under Hydrothermal Condition
Dewetting Behavior of Hydrogen Bonded Polymer Complex Film under Hydrothermal Condition作者机构:State Key Laboratory for Modification of Chemical Fibers and Polymer Materials Center for Advanced Low-dimension Materials College of Material Science and Engineering Donghua University Department of Polymer Science The University of Akron
出 版 物:《Chinese Journal of Polymer Science》 (高分子科学(英文版))
年 卷 期:2018年第36卷第9期
页 面:1036-1042页
核心收录:
学科分类:08[工学] 0817[工学-化学工程与技术] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学]
基 金:financially supported by the National Natural Science Foundation of China(No.51373032)
主 题:Hydrogen-bonding Polymer complex Dewetting
摘 要:Hydrogen-bonded polymer complex films with the thickness ranging from 50 nm to 2400 nm were prepared by layer-by-layer (LbL) assembly of poly(2-ethyl-2-oxazoline) (PEOX) and poly(acrylic acid) (PAA). The dewetting behavior of PEOX/PAA films under hydrothermal condition was investigated. It was found that the dewetting occurred at solid-liquid interface, and the typical morphologies such as holes, irregular cellular structure, and droplets were observed. Atomic force microscopy (AFM) revealed the initial rupture of the film. Microscopic Raman and infrared (IR) imaging demonstrated that the PEOX and PAA chains remained association during the dewetting process.