Microstructure and mechanical properties of WC-(Ti,M)(C,N)-Co cemented carbides with different nitrogen contents
Microstructure and mechanical properties of WC-(Ti,M)(C,N)-Co cemented carbides with different nitrogen contents作者机构:School of Materials Science and EngineeringSichuan UniversityChengdu610065China
出 版 物:《Rare Metals》 (稀有金属(英文版))
年 卷 期:2022年第41卷第10期
页 面:3530-3538页
核心收录:
学科分类:08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0802[工学-机械工程] 0703[理学-化学]
基 金:financially supported by the National Important and Special Project of China (No.2013ZX04009022) Sichuan Provincial Science Research Program of China (No. 2013GC0136)
主 题:Cemented carbides Solid-solution powders Nitrogen content Mechanical properties
摘 要:Three kinds of(Ti,M)(C_(1-x),N_(x))(M=Ta,Nb,W) quaternary solid-solution powders with various nitrogen contents were synthesized by carbothermal reductionnitridation(CRN) *** of nitrogen content on the microstructure and mechanical properties of WC-(Ti,M)(C_(1-x),N_(x))-Co cemented carbides fabricated by sinterhot isostatic pressing(HIP) were systematically investigated in this *** results show that the nitrogen content in the carbonitride raw powders strongly influences the morphology,the grain size and the compositions of the cemented *** the cemented carbides with different nitrogen contents have a similar microstructural appearance:weak core-rim structure consisting of solidsolution phase embedded in WC-Co *** is also observed that the carbonitride solid solution could somewhat reduce the WC grain growth,and the effectiveness of refining and the rim thickness are sensitively related to the nitrogen content of(Ti,M)(C_(1-x),N_(x)) solid *** addition,with an increase in the nitrogen content,mechanical properties of these hard metals are enhanced,which were discussed in terms of the constituent,the microstructure and the solution behavior of the carbonitride solid solutions.