Crystallization, Mechanical and Flame-retardant Properties of Poly(lactic acid) Composites with DOPO and DOPO-POSS

作     者：Lin Jia Wen-Chao Zhang Bin Tong Rong-Jie Yang 

作者机构：National Engineering Research Center of Flame Retardant Materials School of Materials Science and Engineering Beijing Institute of Technology 

出 版 物：《Chinese Journal of Polymer Science》 (高分子科学（英文版）)

年 卷 期：2018年第36卷第7期

页      面：871-879页

核心收录：

学科分类：081704[工学-应用化学] 07[理学] 08[工学] 0817[工学-化学工程与技术] 070305[理学-高分子化学与物理] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0703[理学-化学] 

主　　题：Poly(lactic acid) DOPO-POSS Crystallization Mechanical property Flame retardancy 

摘      要：Poly（lactic acid） （PLA） composites with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide （DOPO） and DOPO- containing polyhedral oligomeric silsesquioxane （DOPO-POSS） were prepared via melting extrusion and injection molding. The crystallization, mechanical, and flame-retardant properties of PLA/DOPO and PLA/DOPO-POSS were investigated by differential scanning calorimetry （DSC）, X-ray diffraction （XRD）, tensile testing, thermogravimetric analysis （TGA）, limiting oxygen index （LOI）, and cone calorimeter test. The DSC results showed that the DOPO added could act as a plasticizer as reflected by lower glass transition temperature and inhibited crystallization of part of the PLA; the DOPO-POSS acted like a filler in the PLA matrix and slightly improved the crystallinity of the PLA matrix. The XRD and DSC analyses indicated that the PLA composites by cold molding injection were amorphous, and the PLA composites following a heat treatment in an oven at 120 ℃for 30 min achieved crystallinity. All the PLA and its composites after heat treatment had improved mechanical properties. The thermogravimetric analysis （TGA） tests showed that the PLA, DOPO and DOPO-POSS decomposed separately in the PLA/DOPO and PLA/DOPO-POSS, respectively. The cone calorimeter tests offered clear evidence that addition of the DOPO-POSS resulted in an evident reduction of 25% for the peak of heat release rate （p-HRR）. It was also confirmed that the crystalline flame-retardant PLA composites after heat treatment had better flame retardant properties than the amorphous PLA composites prepared by the cold molding.