Investigation of Solidification and Segregation Characteristics of Cast Ni-Base Superalloy K417G

作     者：Li Gong Bo Chen Zhanhui Du Mengshu Zhang Ruichang Liu Kui Liu 

作者机构：Institute of Metal Research Chinese Academy of Sciences 

出 版 物：《Journal of Materials Science & Technology》 (材料科学技术（英文版）)

年 卷 期：2018年第34卷第3期

页      面：541-550页

核心收录：

学科分类：08[工学] 0817[工学-化学工程与技术] 0806[工学-冶金工程] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学（可授工学、理学学位）] 0702[理学-物理学] 

主　　题：K417G superalloy Solidification characteristics Segregation Isothermal solidification Thermo Calc simulation 

摘      要：Differential scanning calorimetry （DSC） analysis, isothermal solidification experiment and Thermo-Calc simulation were employed to investigate solidification characteristics of K417G Ni-base superalloy. Elec- tron probe microanalysis （EPMA） was employed to analyze the segregation characteristics. Liquidus, solidus and the formation temperatures of main phases were measured. In the process of solidification, the volume fraction of liquid dropped dramatically in the initial stage, while the dropping rate became very low in the final stage due to severe segregation of positive segregation elements into the residual liquid. The solidification began with the formation of primary γ. Then with solidification proceeding, Ti and Mo were enriched in the liquid interdendrite, which resulted in the precipitation of MC carbides in the interdendrite. A1 accumulated into liquid at the initial stage, but gathered to solid later due to the precipitation of γ/γ＇ eutectic at the intermediate stage of solidification. However, Co tended to segregate toward the solid phase. In the case of K417G alloy, combining DSC analysis and isothermal solidification experiment is a good way to investigate the solidification characteristics. Thermo-Calc simulation can serve as reference to investigate K417G alloy.