Preparation of TiAl alloy powder by high-energy ball milling and diffusion reaction at low temperature
Preparation of TiAl alloy powder by high-energy ball milling and diffusion reaction at low temperature作者机构:Institute for Advanced Material and Technology University of Science and Technology Beijing
出 版 物:《Rare Metals》 (稀有金属(英文版))
年 卷 期:2018年第37卷第1期
页 面:21-25页
核心收录:
学科分类:08[工学] 0806[工学-冶金工程] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0703[理学-化学] 0702[理学-物理学]
基 金:financially supported by the National Natural Science Foundation of China (No. 51274039) the Guangdong Foundation of Research (No. 2011A090200091)
主 题:High energy ball milling Titanium hydride powder Titanium powder TiAl alloy powder Diffusion reaction
摘 要:In this paper, TiAl alloy powders were prepared successfully by high-energy ball milling and diffusion reaction in vacuum at low temperature. The titanium powder, aluminum powder, and titanium hydride powder were used as raw materials. The samples were characterized by scanning electron microscopy(SEM), X-ray diffraction(XRD), field-emission scanning electron microscopy(FESEM), and differential thermal analysis(DTA). The results show that the alloy powders with the main intermetallic compounds of TiAl are obtained using Ti-Al powders and TiH2-Al powders after heated for 2 h at 500 ℃,3 h at 600 ℃,and 3 h at 750 ℃,respectively.The average grain sizes of alloy powder are about 45 and20 μm with irregular shape, respectively. The prepared TiAl alloy powders are relatively pure, and the average quality content of oxygen in the alloy powders is0.33 wt%. The forming process of alloy powder contains both the diffusion reaction of Ti and Al,which gives priority to the diffusion reaction of aluminum.