Influence of ECAP as grain refinement technique on microstructure evolution, mechanical properties and corrosion behavior of pure aluminum

作     者：Mohamed Ibrahim ABD EL AAL M.M.SADAWY Mohamed Ibrahim ABD EL AAL;M.M.SADAWY

作者机构：Mechanical Design and Production Department Faculty of Engineering Zagazig University Mining and Petroleum Engineering Department Al-Azhar University 

出 版 物：《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报（英文版）)

年 卷 期：2015年第25卷第12期

页      面：3865-3876页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

主　　题：equal channel angular pressing(ECAP) microstructure mechanical properties corrosion resistance passive film pitting 

摘      要：Pure aluminum samples were processed by equal channel angular pressing（ECAP） up to 10 passes at room temperature. The effects of the ECAP number of passes on the microstructure evolution, the mechanical properties, deformation homogeneity and corrosion behavior of the processed samples were fully investigated. The imposed strain resulted in an obvious reduction in the grain size from 390 μm before ECAP down to 1.8, 0.4, and 0.3 μm after ECAP up to 2, 4 and 10 passes, respectively. The microhardness, deformation homogeneity and tensile strength were increased while the elongation decreased with the increase of ECAP number of passes. Immersion tests, open circuit potential, Tafel polarization, cyclic polarization and potentiostatic measurements in 3.5% Na Cl solution revealed an obvious improvement in the corrosion resistance of ECAP processed samples compared with the as-cast sample. The increase of the number of passes can be used successfully in producing ultra-fine grained（UFG） bulk pure aluminum sample with a high misorientation angle, reasonably high mechanical properties and corrosion resistance.