Effect of sintering temperature on the microstructure and properties of foamed glass-ceramics prepared from high-titanium blast furnace slag and waste glass

作     者：Chang-hong Chen Ke-qin Feng Yu Zhou Hong-ling Zhou 

作者机构：School of Manufacturing Science and Engineering Sichuan University 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2017年第24卷第8期

页      面：931-936页

核心收录：

学科分类：083002[工学-环境工程] 0830[工学-环境科学与工程（可授工学、理学、农学学位）] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：financially supported by the Science and Technology Support Program of Sichuan Province (No.2014GZ0011) the Industry Promotion Project of Panzhihua City, China (No.2012CY-C-2) 

主　　题：foamed glass-ceramics sintering temperature blast furnace slag waste glass crystallization 

摘      要：Foamed glass-ceramics were prepared via a single-step sintering method using high-titanium blast furnace slag and waste glass as the main raw materials The influence of sintering temperature(900–1060℃) on the microstructure and properties of foamed glass-ceramics was studied. The results show that the crystal shape changed from grainy to rod-shaped and finally turned to multiple shapes as the sintering temperature was increased from 900 to 1060℃. With increasing sintering temperature, the average pore size of the foamed glass-ceramics increased and subsequently decreased. By contrast, the compressive strength and the bulk density decreased and subsequently increased. An excessively high temperature, however, induced the coalescence of pores and decreased the compressive strength. The optimal properties, including the highest compressive strength(16.64 MPa) among the investigated samples and a relatively low bulk density(0.83 g/cm^3), were attained in the case of the foamed glass-ceramics sintered at 1000℃.