The Dielectric Properties and Preparation Method of BaTiO_3/PVDF 0-3 Composites

作     者：熊传溪 XIONG Chuan-xi 1)CHEN Juan 1)DONG Li-jie 2)NAN Ce-wen 2)ZHANG Xuan 1)Wuhan University of Technology 2)Tsinghua University

作者机构：WuhanUniversityofTechnoloy 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2002年第17卷第4期

页      面：82-85页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：theNationalNaturalScienceFoundationofChina (No .5 0 172 0 10 ) 

主　　题：BaTiO 3/PVDF dielectric constant dielectric loss 

摘      要：A series of 0-3 composites of the polyvinylidene fluoride (PVDF) and BaTiO 3 was *** 3 was modified with titanate coupling *** dielectric properties and the interfacial interaction of composites by different preparation methods were examined and *** result shows that the relative dielectric constant ε of the composite prepared in solution has a maximum value at about 70% weight fraction of BaTiO 3 and the dielectric loss tanδ increases rapidly when the fraction exceeds 70%.For the composite prepared in melt,the relative dielectric constant ε almost reaches a maximum value at about 60% weight fraction of BaTiO 3 and the dielectric loss is comparatively *** dielectric properties of composites are improved by using a coupling agent.