Low Temperature Synthesis of Nano Porous 12CaO?7Al_2O_3 Powder by Hydrothermal Method
Low Temperature Synthesis of Nano Porous 12CaO?7Al_2O_3 Powder by Hydrothermal Method作者机构:Ningbo Institute of Material Technology and EngineeringChinese Academy of Sciences
出 版 物:《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报(材料科学英文版))
年 卷 期:2016年第31卷第6期
页 面:1201-1205页
核心收录:
学科分类:07[理学] 070205[理学-凝聚态物理] 0805[工学-材料科学与工程(可授工学、理学学位)] 0702[理学-物理学]
基 金:Funded by the National Natural Science Foundation of China(No.21377063) the Zhejiang Natural Science Foundation(No.LY15F040004) the Program for Ningbo Key Laboratory of Silicon and Organic Thin Film Optoelectronic Technologies
主 题:C12A7 hydrothermal method low temperature nano pore
摘 要:Single-phase insulating 12CaO?7Al_2O_3(C12A7) powder was synthesized using an optimized hydrothermal method. Pure phase of C12A7 was got at a comparatively lower temperature(c.a. 300 ℃) than that has been previously reported. The crystallite size of the synthesized C12A7 powder was 7±2 nm. The surface area values calculated for all the samples at a synthesis temperature range of 250-800 ℃ for 5 h were in the range of about 19-24 m^2/g, with pore sizes of 12-20 nm. This low-temperature-based synthetic strategy along with nano porous structures and a high surface area value can facilitate catalyst application.