YbF_3/SiO_2 Fillers as Radiopacifiers in a Dental Adhesive Resin
YbF3/SiO2 Fillers as Radiopacifiers in a Dental Adhesive Resin作者机构:Technology Development CenterEngineering of MaterialFederal University of Pelotas Biomaterials Development and Control CenterSchool of DentistryFederal University of Pelotas Department of Analytical and Inorganic ChemistryIQGFederal University of Pelotas
出 版 物:《Nano-Micro Letters》 (纳微快报(英文版))
年 卷 期:2012年第4卷第3期
页 面:189-196页
核心收录:
学科分类:081702[工学-化学工艺] 0808[工学-电气工程] 0809[工学-电子科学与技术(可授工学、理学学位)] 0817[工学-化学工程与技术] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0702[理学-物理学]
基 金:the Brazilian National Council for Scientific and Technological Development for financial support FAPERGS CNPq and CAPES
主 题:Radiopacifier YbF3/SiO2 Dental adhesive resin Composite
摘 要:The objective of this study was to evaluate the effect of functionalizing a dental adhesive resin with YbF_3/SiO_2 fillers for use as *** of YbF_3/SiO_2 were obtained with the high-energy mechanical milling method and characterized by both physical and chemical *** characterization,the particles were sieved and silanized prior to being incorporated into an adhesive *** stability of the particle suspension was then *** light activation,the radiopacity,degree of conversion,flexural strength and elastic modulus were *** dental adhesive resins with 10 and 15 wt% of filler provided satisfactory radiopacity,while flexural strength and elastic modulus were not *** degree of conversion was statistically lower than that of the control(p0.05).The method used for incorporating the tested ytterbium fluoride/silicon dioxide particles at concentrations of 10 and 15 wt% was shown to be feasible for the development of a radiopaque dental adhesive system.