Strength and Microstructure of Mortar Containing Glass Powder and/or Glass Aggregate

作     者：刘数华 WANG Shu ZHOU Wei LI Lihua XIAO Henglin WEI Jianpeng TANG Wan 

作者机构：State Key Laboratory of Water Resources and Hydropower Engineering Science Wuhan University Wuhan 430072 China China Construction Ready Mixed Concrete Co. Ltd. Wuhan 430000 China School of Civil Engineering and Architecture Hubei University of Technology Wuhan 430068 China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2016年第31卷第6期

页      面：1302-1310页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the National Natural Science Foundation of China(51208391) the National Basic Research Program of China(973 Program,2013CB035901) 

主　　题：glass powder glass aggregate mortar strength microstructure 

摘      要：The compressive strength of mortar containing glass powder（GP） and/or glass aggregate（GA） was tested, and its microstructure was also studied by thermogravimetric and differential thermal analysis（TG-DTA）, scanning electron microscopy（SEM）, energy dispersive spectroscopic analysis（EDX）, and X-ray diffraction（XRD） techniques. The incorporation of GA would decrease the compressive strength of the mortar in the absence of GP. Incorporating both GA and GP could change the hydration environment, promote pozzolanic reaction of GP and improve the compressive strength. GP does not lead to but can effectively control ASR（Alkali Silica Reaction）. GP and GA do not transform the type of hydrates, but have a great influence on the amounts of hydration products, and generate more calcium silicate hydrate（C-S-H gel） with lower Ca/Si ratio. GP and GA with good gradation will make the microstructure denser.