Synthesis of nickel aluminate nanoceramic compound from aluminum and nickel carbonate by mechanical alloying with subsequent annealing

作     者：M.JAVANMARDI R.EMADI H.ASHRAFI M. JAVANMARDI;R. EMADI;H. ASHRAFI

作者机构：Department of Materials Engineering Isfahan University of Technology 

出 版 物：《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报（英文版）)

年 卷 期：2016年第26卷第11期

页      面：2910-2915页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：nickel aluminate nanoceramic ball-milling annealing 

摘      要：The aim of present work was to produce pure nickel aluminate （NiAl2O4） nanoceramic compound by high energy millingof nickel carbonate （NiCO3） and aluminum （Al） powders followed by annealing. Phase composition, thermal behavior, morphologyand microstructure of powder samples were characterized by means of X-ray diffraction, differential scanning calorimeter,thermogravimetric analysis, scanning electron microscopy and transmission electron microscopy. The results showed that formationof NiAl2O4 spinel compound from NiCO3 and Al powders took place in three steps： oxidation of Al to Al2O3, decomposition ofNiCO3 to NiO and CO2, and finally the solid state reaction between Al2O3 and NiO. It was also demonstrated that single phaseNiAl2O4 spinel compound can be produced by 5 h of mechanical milling with subsequent annealing of NiCO3/Al mixture at 900 Cfor 2 h, which is 冾 500 C lower than the temperatures used in the traditional solid state methods. The particle diameter of theproduced NiAl2O4 spinel compound was found to be less than 100 nm as measured by transmission electron microscopy.