Effects of Ultrasonic Treatment on Microstructure and Mechanical Properties of Semisolid Sn-52Bi Alloy

作     者：胡永俊 郑辉庭 

作者机构：School of Material and Energy Guangdong University of Technology Guangzhou 510006 China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2016年第31卷第5期

页      面：1063-1067页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：Funded by the National Natural Science Foundation of China(No.51104049) 

主　　题：semisolid Sn 52Bi ultrasonic treatment microstructure mechanical properties 

摘      要：The effects of ultrasonic vibration temperature on the microstructure of semisolid Sn-52 Bi alloy and mechanical properties were investigated. The results show that the microstructure and mechanical properties are improved obviously after the ultrasonic treatment. Nearly round and uniformly distributed primary Sn phase particles were obtained under the cavitation and acoustic streaming caused by ultrasonic treatment. The best effects of ultrasonic treatment on microstructure and mechanical properties were obtained with the ultrasonic vibration for 120 s at 140 ℃. The elongation of semisolid Sn-52 Bi alloy treated by ultrasonic vibration for 120 s at 140 ℃ was 42% and increased by 156.09% compared to conventional liquid casting Sn-52 Bi alloy without ultrasonic vibration. It is a feasible and effective method to adopt the semisolid metal forming technology assisted with ultrasonic vibration to improve the ductility of Sn-Bi alloys.