Germanium separation and purification by leaching and precipitation

作     者：Saeid Bayat Sajjad Aghazadeh Mohammad Noaparast Mahdi Gharabaghi Behrooz Taheri 

作者机构：School of Mining Engineering College of Engineering University of Tehran 

出 版 物：《Journal of Central South University》 (中南大学学报（英文版）)

年 卷 期：2016年第23卷第9期

页      面：2214-2222页

核心收录：

学科分类：080903[工学-微电子学与固体电子学] 0809[工学-电子科学与技术（可授工学、理学学位）] 08[工学] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：supported by Zanjan Calcimin Zinc Company 

主　　题：experimental design di-ammonium oxalate monohydrate germanium leaching, tannic acid 

摘      要：In this research work, extraction and purification of germanium from zinc leach residues(ZLR) were investigated. The results of ICP, XRF, and atomic adsorption spectroscopy(AAS) tests show that contents of germanium, iron, lead, and zinc within the leaching residue were 105×10^(-6), 3.53%, 10.35%, and 8.8%, respectively. XRD results indicate that the main minerals were in different forms of sulfates(CaSO_4·2H_2O, PbSO_4 and ZnSO_4·6H__2O), silicate(SiO_2), and oxide(Fe_2O_3). Dissolution of leaching filter cake was carried out using 5 parameters and each in 4 levels(acid concentration, temperature, time, liquid-to-solid ratio, and stirring speed) by Taguchi method(L_(16)), and then optimization of the effective parameters by response surface method. Under optimum conditions, zinc and germanium dissolution efficiencies were 88.71% and 8%, respectively. Leaching tests with sulfuric acid(added di-ammonium oxalate monohydrate) and hydrochloric acid(HCl) on the residues obtained from previous-stage sulfuric acid dissolution, yielded germanium and iron recoveries of 83%, 88%, 40%, and 90%, respectively. Thus, leaching experiment with sulfuric acid(added di-ammonium oxalate monohydrate) was superior to that with hydrochloric acid due to high and low extraction amounts of germanium and iron, respectively. Precipitation experiments revealed that germanium purification with tannic acid presented a better result compared to sodium hydroxide and ammonia. Under optimum conditions, contents of germanium and iron in the solution after precipitation were 0.1505% and 14.7% with precipitation yields of 91% and 52%, respectively.