The Effect of Bi_2O_3 on the Structure and Microwave Dielectric Properties of Ba_(6-3x)Nd_(8+2x)Ti_(18)O_(54)System(x=2/3)

作     者：LI Yuan WU Shunhua SU Hao WANG Xiaoyong 

作者机构：Institute of Electronics and Information Engineering Tianjin University Tianjin 300072 China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2008年第23卷第2期

页      面：143-146页

核心收录：

学科分类：080801[工学-电机与电器] 0808[工学-电气工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：the Natural Science Foundation of Tianjin(No.06YFJMJC01000) 

主　　题：BNT Bi2O3 dielectric constant temperature coefficient Q value 

摘      要：The structures and dielectric properties of Ba6-3xNd8＋2xTi18O54 system（x=2/3） doped with different contents of Bi2O3, whose final molecular formula is Ba6-3x（Nd1-yBiy）8＋2xTi18O54 were investigated. It is indicated that the dielectric constant increases greatly whereas Q value（f0=4 GHz） decreases with the increase of Bi2O3 content. However, the temperature coefficient could be controlled below 0±30×10^-6/℃ in the experiment. These phenomena are related to the appearance of a new phase, Bi4Ti3O12, which has high dielectric constant. Also, that Bi^3＋（0.13 nm） substitutes for Nd^3＋（0.099 5 nm） will increase the unit cell volume, which will lead to the enlargement of the octahedron B site occupied by Ti^4＋. So the spontaneous polarization of Ti^4＋ ions will be strengthened. Besides, Bi^3＋ will fill up some vacancies which Ba^2＋ or Nd^3＋ ions leave in two A1 sites and four A2 sites. More positive ions polarize, which also contributes to higher dielectric constant. The samples got with the optimium properties are sintered at 1 200 ℃ for 4 h, when y=0.25, ε≈110, Q≈5 400（f0=4 GHz）, TCC=-4.7×10^-6/℃; When y=0.3, ε≈120, Q≈5 000（f0=4 GHz）, TCC=-24×10^-6/℃.