Structural,Morphological and Electrical Properties of In-Doped Zinc Oxide Nanostructure Thin Films Grown on p-Type Gallium Nitride by Simultaneous Radio-Frequency Direct-Current Magnetron Co-Sputtering

作     者：R.Perumal Z.Hassan R.Saravanan 

作者机构：Institute of Nano-Optoelectronics Research and TechnologySchool of PhysicsUniversiti Sains Malaysia Department of PhysicsUniversity College of Engineering PattukkottaiAnna University Chennai 

出 版 物：《Chinese Physics Letters》 (中国物理快报（英文版）)

年 卷 期：2016年第33卷第6期

页      面：77-80页

核心收录：

学科分类：08[工学] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0704[理学-天文学] 

基　　金：Supported by the RU Top-Down under Grant No 1001/CSS/870019 

主　　题：ZnO of Structural,Morphological and Electrical Properties of In-Doped Zinc Oxide Nanostructure Thin Films Grown on p-Type Gallium Nitride by Simultaneous Radio-Frequency Direct-Current Magnetron Co-Sputtering that by were been In EDX on 

摘      要：Zinc oxide （ZnO） is one of the most promising and frequently used semiconductor materials. In-doped nanos- tructure ZnO thin films are grown on p-type gallium nitride substrates by employing the simultaneous rf and dc magnetron co-sputtering technique. The effect of In-doping on structural, morphological and electrical properties is studied. The different dopant concentrations are accomplished by varying the direct current power of the In target while keeping the fixed radio frequency power of the ZnO target through the co-sputtering deposition technique by using argon as the sputtering gas at ambient temperature. The structural analysis confirms that all the grown thin films preferentially orientate along the c-axis with the wurtzite hexagonal crystal structure without having any kind of In oxide phases. The presenting Zn, 0 and In elements＇ chemical compositions are identified with EDX mapping analysis of the deposited thin films and the calculated M ratio has been found to decrease with the increasing In power. The surface topographies of the grown thin films are examined with the atomic force microscope technique. The obtained results reveal that the grown film roughness increases with the In power. The Hall measurements ascertain that all the grown films have n-type conductivity and also the other electrical parameters such as resistivity,mobility and carrier concentration are analyzed.