High-temperature properties and microstructure of Mo microalloyed ultra-high-strength steel

作     者：Qi-hang Han Yong-lin Kang Xian-meng Zhao Lu-feng Gao Xue-song Qiu 

作者机构：School of Materials Science and Engineering University of Science and Technology Beijing Beijing 100083 China State Key Laboratory for Advanced Metals and Materials University of Science and Technology Beijing Beijing 100083 China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2011年第18卷第4期

页      面：407-412页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：supported by the National High-tech Research and Development Program of China (No.2009AA03Z518) 

主　　题：high strength steels high temperature properties microstructure molybdenum thermodynamics 

摘      要：The high-temperature mechanical properties and microstructure of forging billets of C-Si-Mn-Cr and C-Si-Mn-Cr-Mo ultra-high-strength cold-rolled steels（tensile strength≥1000 MPa,elongation≥10%） were *** the comparison of reduction in area and hot deformation resistance at 600-1300°C,the Mo-containing steel was found to possess a higher strength and a better plasticity than the Mo-free *** equilibrium phase diagram and atom fraction of Mo in different phases at different temperatures were calculated by Thermo-Calc software（TCW）.The results analyzed by using transmission electron microscopy and TCW show that precipitates in the Mo-containing steel are primarily M23C6,which promote pearlite *** experimental data also show that a lower ductility point existing in the Mo-free steel at 850°C is eliminated in the Mo-containing *** is mainly due to the segregation of Mo at grain boundaries investigated by electron probe microanalysis（EPMA）,which improves the strength of grain boundaries.