Influence of aluminum solid fraction on property of steel-mushy aluminum bonding plate

作     者：Peng Zhang Yunhui Du Xueping Ren Yonglin Kang Hanwu Liu Jianzhong Cui Limin Ba(Material Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China)(Metal Forming Department, Northeastern University, Shenyang 110006 

作者机构：Material Science and Engineering School University of Science and Technology Beijing Beijing 100083 China Metal Forming Department Northeastern University Shenyang 110006 China Anshan Automobile Fittings Factory Anshan 114014 China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：1999年第13卷第3期

页      面：193-195页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：steel-mushy aluminum bonding plate solid fraction interfacial shear strength 

摘      要：The interfacial shear property of steel-mushy aluminum bonding plate was studied, and the relationship between aluminum solid fraction and the interfacial shear strength of bonding plate was determined. The results showed that when aluminum solid fraction is 34.3 %, the maximum interfacial shear strength of bonding plate is 71 .0 MPa.