Electro-spinning Antimicrobial N-halamine Modified Poly(vinyl alcohol)Nanofibers

作     者：姜潜远 任学宏 黄东时 

作者机构：Key Laboratory of Eco-textiles of Ministry of EducationCollege of Textiles and ClothingJiangnan University Department of Poultry ScienceAuburn University 

出 版 物：《Journal of Donghua University(English Edition)》 (东华大学学报（英文版）)

年 卷 期：2014年第31卷第1期

页      面：44-49页

核心收录：

学科分类：0821[工学-纺织科学与工程] 08[工学] 082103[工学-纺织化学与染整工程] 

主　　题：poly(vinyl alcohol)(PVA) antimicrobial nanofiber electro-spinning N-halamine 

摘      要：Antimicrobial poly( vinyl alcohol)( PVA) nanofibrous composites were prepared by adding 3-( 2,3-dihydroxypropyl)-5,5-dimethylimidazolidine-2,4-dione( N-halamine diol) to the PVA solution using electro-spinning technique upon curing and exposure to diluted sodium hypochlorite. Scanning electron microscopy( SEM) demonstrates that PVA nanofibers formed with diameters of( 255 ±94) nm. Cross-linked PVA nanofibers with N-halamine diol precursor and 1,2,3,4-butanetetracarboxylic( BTCA) showed good water resistance. The chlorinated PVA nanofibrous mats completely inactivated Staphylococcus aureus( Gram-positive) and Escherichia coli O157: H7( Gram-negative) with 7 log reductions( the reduction of the bacterial concentration in logarithm) within 5min and 1 min of contact time,respectively.