SINTERING BEHAVIOR OF Cu-Al ALLOY POWDER

作     者：TIAN Sugui SHAO Huimeng ZHOU Longjiang LI Tiefan YANG Hongcai HAO Shiming(Shenyang Polytechnic University, China) (State Key Laboratory of Corrosion and Protection. Institute of Corrosion and Protection of Metals. Chinese Academy of Sciences, Shenyan 

作者机构：Shenyang Polytechnic Univ Shenyang China 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：1995年第8卷第3期

页      面：231-234页

核心收录：

学科分类：0810[工学-信息与通信工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0812[工学-计算机科学与技术（可授工学、理学学位）] 

主　　题：transient liquid phase sintering surface reaction diffusing Cu-Al alloy 

摘      要：The dynamic behaviour of transient liquid phase during sintering 5wt% Al-Cu alloy compacts with green density of 7.56g/cn￣3 is observed by means of high temperature metallographic microscopy. The structures and precipitating order of the phases are identified by means of DTA, TEM and composion analysis at the definite point and phase diagram. The results show that little Al-rich liquid phase resulting from eutectic reaction flows into the capillaries in Cu powder, because the peritectic reactions exhausts the liquid in high density compact,the composition homogenization needs longer sintering time. The remainder γ2-phase is discovered at place of the neck of sintered Cu particle and has a crystallographic relationship of (111)_(Cu)∥(033)_γ_2 after alloy is sintered at 900 ℃for 3h.