Interface structure and formation mechanism of diffusion-bonded joints of TiAl-based alloy to titanium alloy

作     者：刘会杰 冯吉才 

出 版 物：《China Welding》 (中国焊接（英文版）)

年 卷 期：2000年第9卷第2期

页      面：36-40页

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：diffusion bonding interface structure formation mechanism TiAl based alloy titanium alloyH 

摘      要：Vacuum diffusion bonding of a TiAl based alloy (TAD) to a titanium alloy (TC2) was carried out at 1 273 K for 15～120 min under a pressure of 25 MPa . The kinds of the reaction products and the interface structures of the joints were investigated by SEM, EPMA and XRD. Based on this, a formation mechanism of the interface structure was elucidated. Experimental and analytical results show that two reaction layers have formed during the diffusion bonding of TAD to TC2. One is Al rich α(Ti)layer adjacent to TC2,and the other is (Ti 3Al+TiAl)layer adjacent to TAD,thus the interface structure of the TAD/TC2 joints is TAD/(Ti 3Al+TiAl)/α(Ti)/*** interface structure forms according to a three stage mechanism,namely(a)the occurrence of a single phase α(Ti)layer;(b)the occurrence of a duplex phase(Ti 3Al+TiAl)layer;and(c)the growth of the α(Ti)and (Ti 3Al+TiAl)layers.