Preparation, Crystallization and Mechanical Properties of Potassium Aluminosilicate Glass-ceramics

作     者：郑伟宏 黄猛 GAO Zipeng ZHANG Hang YUAN Jian TIAN Peijing PENG Zhigang ZHENG Weihong;HUANG Meng;GAO Zipeng;ZHANG Hang;YUAN Jian;TIAN Peijing;PENG Zhigang

作者机构：State Key Laboratory of Silicate Materials for ArchitecturesWuhan University of TechnologyWuhan 430070China Shahe Research Institute of Glass TechnologyShahe 054100China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2024年第39卷第3期

页      面：587-595页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by State Key Laboratory of Silicate Materials for Ar-chitectures(Wuhan University of Technology)(No.2011DA105356) 

主　　题：leucite glass-ceramic kaliophilite crystallization kinetics 

摘      要：In this study,transparent K_(2)O-Al_(2)O_(3)-SiO_(2)(KAS)glass-ceramics with leucite as the main crystalline phase were prepared by melting-quench method and two-step heat *** effects of SiO_(2)/Al_(2)O_(3) ratio and heat treatment on crystallization and mechanical properties were *** crystallization kinetics and X-Ray Diffraction(XRD)results showed that SiO_(2)/Al_(2)O_(3) ratio and heat treatment system had a direct impact on the crystallization behavior of potassium aluminosilicate *** heat-treated at 680℃/2 h and 780℃/1 h,cracks generated on the surface of the sample with the addition of SiO_(2)/Al_(2)O_(3)=4.8(in mol)due to the huge difference in the coefficient of thermal expansion between glass matrix and *** the addition of SiO_(2)/Al_(2)O_(3)(in mol)was 4,the sample with leucite as the main crystalline phase showed an excellent fracture toughness(1.46 MPa·m^(0.5))after the heat treatment of 680℃/2 h and 780℃/5 *** there was a phase transformation from kaliophilite to *** crystalline phases of the sample heat-treated at 680℃/8 h and 780℃/1 h were leucite and kaliophilite,which resulted in the visible light transmittance of 63%and the fracture toughness of 0.91 MPa·m^(0.5).Furthermore,after the heat treatment of 680℃/2 h and 780℃/5 h,the main crystalline phase of the sample with SiO_(2)/Al_(2)O_(3)=3.2(in mol)was still *** leucite only grows on the surface of the sample and is hard to grow inward,it is hard to achieve the bulk crystallization of leucite in the sample with SiO_(2)/Al_(2)O_(3)=3.2(in mol).