Effect of pre-twinning and heat treatment on formability of AZX311 Mg alloy
作者机构:Department of Mechanical EngineeringIndian Institute of Technology JodhpurKarwarJodhpur 342030RajasthanIndia Department of Metallurgical and Materials EngineeringIndian Institute of Technology JodhpurKarwarJodhpur 342030RajasthanIndia Energy Materials Research CenterKorea Institute of Science and Technology(KIST)5 Hwarang-roSeongbuk-guSeoul 02792Republic of Korea Department of Advanced Components and Materials EngineeringSunchon National University255 Jungang-roSuncheonJeonnam 57922Republic of Korea
出 版 物:《Journal of Magnesium and Alloys》 (镁合金学报(英文))
年 卷 期:2024年第12卷第3期
页 面:1154-1169页
核心收录:
学科分类:080503[工学-材料加工工程] 0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0802[工学-机械工程] 080201[工学-机械制造及其自动化]
基 金:supported by the Science and Engineering Research Board(SERB) a statutory body of the Department of Science&Technology(DST) Government of India through the Start-up Research Grant(SRG)scheme(File No.SRG/2020/000341)
主 题:Mg alloys Pre-twinning Texture Formability EBSD.
摘 要:In this study,the effects of pre-strain-induced tensile twins(TTWs)and controlled heat treatment on the formability behavior of AZX311 Mg alloy sheets were investigated.A 4%compressive strain was applied to pre-strain the sheets using the in-plane compression(IPC)technique along the rolling direction(RD)to introduce *** pre-strained(PS)samples were subsequently heat-treated at 250℃,350℃,and 400℃ independently for 1 hr,and are termed as PSA1,PSA2,and PSA3,*** cupping tests were conducted to assess the formability of the sheet samples under different initial *** results showed that the PS sample heat-treated at 250℃ for 1hr exhibited a decrease in the Erichsen index(IE)compared to the as-rolled sample,whereas PSA2 and PSA3 samples showed an increase in IE *** analysis revealed that most of the TTWs generated through pre-twinning were stable at 250℃;however,the twin volume fraction reduced to 41%at 350℃ compared to the PS samples due to enhanced thermal activity at that ***,PSA2 samples showed severe grain coarsening in some areas of the sample,and the fraction of such grains increased in the PSA3 *** stretch formability(IE value)of PSA2 samples showed a 32.3%increase compared to the as-rolled ***,the analysis of the deformed specimen at failure under the Erichsen test indicated that considerable detwinning occurs in the PS and PSA1 samples,whereas dislocation slip activity dominates in the PSA2 and PSA3 samples during stretch *** from detwinning and dislocation slip,deformation twins were also observed in all samples after the Erichsen ***,this work highlights the importance of texture control and its underlying mechanisms via pre-twinning followed by heat treatment and their impact on the room temperature(RT)stretch formability of AZX311 Mg alloy sheets.