Effect of overheating-induced minor addition on Zr-based metallic glasses
Effect of overheating-induced minor addition on Zr-based metallic glasses作者机构:Institute of PhysicsChinese Academy of SciencesBeijing 100190China Center of Materials Science and Optoelectronics EngineeringUniversity of Chinese Academy of SciencesBeijing 100049China School of Physical SciencesUniversity of Chinese Academy of SciencesBeijing 100049China Songshan Lake Materials LaboratoryDongguan 523808China
出 版 物:《Chinese Physics B》 (中国物理B(英文版))
年 卷 期:2024年第33卷第3期
页 面:118-125页
核心收录:
学科分类:08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0702[理学-物理学]
基 金:The work was financially supported by the National Key Research and Development Program of China(Grant Nos.2018YFA0703600,2021YFA0716302,and 2021YFA0718703) the National Natural Science Foundation of China(Grant Nos.51825104 and 52192602) China Postdoctoral Science Foundation(Grant No.2022T150691)
主 题:metallic glass thermal properties melt treatment overheating oxygen content
摘 要:Melt treatment is well known to have an important influence on the properties of metallic glasses(MGs).However,for the MGs quenched from different melt temperatures with a quartz tube,the underlying physical origin responsible for the variation of properties remains poorly *** the present work,we systematically studied the influence of melt treatment on the thermal properties of a Zr50Cu36Al14 glass-forming alloy and unveiled the microscopic ***,we quenched the melt at different temperatures ranging from 1.1Tl to 1.5Tl(Tl is the liquidus temperature)to obtain melt-spun MG ribbons and investigated the variation of thermal properties of the MGs upon *** found that glass transition temperature,Tg,increases by as much as 36 K,and the supercooled liquid region disappears in the curve of differential scanning calorimetry when the melt is quenched at a high temperature up to *** careful chemical analyses indicate that the change in glass transition behavior originates from the incorporation of oxygen and silicon in the molten *** incorporated oxygen and silicon can both enhance the interactions between atoms,which renders the cooperative rearrangements of atoms difficult,and thus enhances the kinetic stability of the MGs.