Efficient Direct Decomposition of NO over La_(0.8)A_(0.2)NiO_(3)(A=K, Ba, Y) Catalysts under Microwave Irradiation
作者机构:School of Materials Science and EngineeringWuhan University of TechnologyWuhan 430070China
出 版 物:《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报(材料科学英文版))
年 卷 期:2024年第39卷第1期
页 面:17-23页
核心收录:
学科分类:081705[工学-工业催化] 08[工学] 0817[工学-化学工程与技术] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学]
主 题:microwave catalysis direct decomposition of NO microwave-absorbing heating ceramics perovskite catalyst
摘 要:La_(0.8)A_(0.2)NiO_(3) (A=K,Ba,Y) catalysts supported on the microwave-absorbing ceramic heating carrier were prepared by the sol-gel *** crystalline phase and the catalytic activity of the La_(0.8)A_(0.2)NiO_(3)catalysts were characterized by XRD and H_(2) temperature-programmed reduction (TPR).The effects of reaction temperature,oxygen concentration,and gas flow rate on the direct decomposition of nitric oxide over the synthesized catalysts were studied under microwave irradiation (2.45 GHz).The XRD results indicated that the La_(0.8)A_(0.2)NiO_(3) catalysts formed an ABO_(3) perovskite structure,and the H_(2)-TPR results revealed that the relative reducibility of the catalysts increased in the order of La_(0.8)K_(0.2)NiO_(3)La_(0.8)Ba_(0.2)NiO_(3)La_(0.8)Y_(0.2)Ni O_(3).Under microwave irradiation,the highest NO conversion amounted to 98.9%,which was obtained with the La_(0.8)K_(0.2)NiO_(3) catalyst at 400℃.The oxygen concentration did not inhibit the NO decomposition on the La_(0.8)A_(0.2)NiO_(3) catalysts,thus the N_(2) selectivity exceeded 99.8%under excess oxygen at 550℃.The NOconversion of the La_(0.8)A_(0.2)NiO_(3) catalysts decreased linearly with the increase in the gas flow rate.