MICROSTRUCTURE AND COMPOSITION OF THE ELECTROLYTIC ETCHED PATTERN GRAINING SURFACE OF Al-Mg-Si ALLOY

作     者：M. Z. An, L. C. Zhao and Z. M. Tu Harbin Institute of Technology, Harbin 150001, China 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：1999年第12卷第5期

页      面：995-1001页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：aluminum alloy electrolytic etching microstructure composition 

摘      要：After electrolytically etched pattern graining surface of aluminum alloy, it is shows that there are porous oxide film containing α Al 2O 3 and α Al 2O 3 by means of SEM XRD and XPS analysis. In the ditches, anodic oxidation makes pore density and diameter larger than other areas, and causes more coloring metal depositing and mutual cross linking. The electrolytically etched pattern surface shows relative deeper color on the ditches and lighter color on other areas, so it can be used for decoration. Electrolytic coloring metal exists in forms of Ag colloid and Ag 2O. Both anodic oxidation and electrolytic coloring affect the surface microstructure of aluminum alloy.