Effect of ZnO,La_(2)O_(3),and YF_(3)on Crystallization and Rehological Behavior of Y_(2)O_(3)-Al_(2)O_(3)-SiO_(2)Glass

作     者：王君 GAO Shengnan ZHENG Qingshuang ZHANG Xiaowei ZHANG Dongliang XIONG Dehua JIN Siqingaowa 王觅堂 焦国豪 WANG Jun;GAO Shengnan;ZHENG Qingshuang;ZHANG Xiaowei;ZHANG Dongliang;XIONG Dehua;JIN Siqingaowa;WANG Mitang;JIAO Guohao

作者机构：School of Materials and ChemistryUniversity of Shanghai for Science and TechnologyShanghai200093China State Key Laboratory of Silicate Materials for ArchitecturesWuhan University of TechnologyWuhan430070China School of Materials and MetallurgyInner Mongolia University of Science and TechnologyBaotou014010China Guangxi Academy of SciencesNanning530000China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2023年第38卷第4期

页      面：753-758页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：the National Natural Science Foundation of China(No.51974168) the Science and Technology Major Project of Inner Mongolia Autonomous Region in China(Nos.2019ZD023 and 2021ZD0028) the State Key Laboratory of Silicate Materials for Architectures(Wuhan University of Technology)(No.SYSJJ2020-08) 

主　　题：Y_(2)O_(3) aluminosilicate glass crystallization viscous activation energy 

摘      要：The effect of substitution La_(2)O_(3)and YF_(3)as network modifiers respectively for Y_(2)O_(3),and ZnO as intermediate oxide for Al_(2)O_(3)on crystallization and viscous behavior of Y_(2)O_(3)-Al_(2)O_(3)-SiO_(2)glass was ***_(2)O_(3)and YF_(3)substitution for Y_(2)O_(3)decreases the melting temperature of studied glass from 1402 to 1346 and 1379℃,and the activation energy of viscous flow decreases from 340 to 250 and 265 kJ/***,ZnO substitution for Al_(2)O_(3)decreases the melting temperature to 1379℃while increases the activation energy of viscous flow to 542 kJ/mol,due to their different role in glass *** ZnO for Al_(2)O_(3)refines and homogenizes the crystals size and lowers crystallinity because the nucleation and crystal growth are depressed by higher activation energy of crystallization and change of crystallization mechanism from bulk crystallization to surface *** of Y_(2)O_(3)by La_(2)O_(3)and YF_(3)respectively also decreases the crystallinity of Y_(2)O_(3)-Al_(2)O_(3)-SiO_(2)glass ceramic due to competitive and hindering effect on the rearranged atoms,structural units and groups required by precipitated two ***,y-Y2Si2O7,precipitation of Y4.67(SiO4)3O,ZnAl_(2)O_(4),and Y3Si3O10F were observed respectively due to incorporation of La_(2)O_(3),ZnO,and YF_(3).