Microstructures and Mechanical Properties of Rapidly Solidified Mg-Al-Zn-MM Alloys

作     者：Yeon-Wook Kim 

作者机构：Department of Advanced Materials Engineering Keimyung UniversityDaegu 704-701Korea 

出 版 物：《Journal of Materials Science & Technology》 (材料科学技术（英文版）)

年 卷 期：2008年第24卷第1期

页      面：89-92页

核心收录：

学科分类：0809[工学-电子科学与技术（可授工学、理学学位）] 07[理学] 070205[理学-凝聚态物理] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0702[理学-物理学] 

主　　题：Mg alloy Gas atomization Misch metal Hot extrusion 

摘      要：Mg-Al-Zn-M M （misch metal） alloy powders were manufactured by inert gas atomization and the characteristics of alloy powders were *** spite of the low fluidity and easy oxidation of the magnesium melt,the spherical powder was made successfully with the improved three piece nozzle systems of gas atomization unit. It was found that most of the solidified powders with particles size of less than 50μm in diameter were single crystal and the solidification structure of rapidly solidified powders showed a typical dendritic morphology because of supercooling prior to *** spacing of secondary denrite arms was deceasing as the size of powders was *** rapidly solidified powders were consolidated by vacuum hot extrusion and the effects of misch metal addition to AZ91 on mechanical properties of extruded bars were also *** extrusion of the rapidly solidified powders,their dendritic structure was broken into fragments and remained as grains of about 3μm in *** Mg-Al-Ce intermetallic compounds formed in the interdendritic regions of powders were finely broken,*** tensile strength and ductility obtained in as-extruded Mg-9 wt pct Al-1 wt pct Zn-3 wt pct MM alloy wereσ-（T.S.） =383 MPa andε=10.6%,*** of these improvements on mechanical properties were resulted from the refined microstructure and second-phase dispersions.