Characteristic of Near-surface Microstructure and Its Effects on the Torsion Performance of Cold Drawn Pearlitic Steel Wires for Bridge Cables
Characteristic of Near-surface Microstructure and Its Effects on the Torsion Performance of Cold Drawn Pearlitic Steel Wires for Bridge Cables作者机构:The State Key Laboratory of Refractories and MetallurgyWuhan University of Science and TechnologyWuhan430081China Baosteel Central Research InstituteWuhan430080China Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of EducationWuhan University of Science and TechnologyWuhan430081China
出 版 物:《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报(材料科学英文版))
年 卷 期:2022年第37卷第5期
页 面:992-999页
核心收录:
学科分类:08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学]
基 金:Funded by the National Key R&D Program of China(No.2017YFB0304801)
主 题:cold-drawn pearlite steel wires torsion performance near-surface microstructure submicron granular ferrite
摘 要:The characteristic of near-surface microstructure and its effects on the torsion performance of cold-drawn pearlitic steel wires for bridge cables were investigated by focused ion beam-scanning electron microscope,transmission electron microscopy and differential scanning *** samples with similar tensile strength before and after hot-dip galvanizing process are,respectively,characterized as delaminated and non-delaminated in torsion test which indicates that the tensile strength is independent of the toughness value(i e,reduction area and torsion ability).It is interesting to find that there exists submicron granular ferrite on near-surface of the wires,which can be attributed to dislocation rearrangement and sub-grains rotation during cold drawing and hot-dip galvanizing *** their distribution can suggest homogeneousness of deformation degree to a certain extent:the closer to the surface of their distribution,the more homogeneous deformation of the *** is a close relationship between the thermal stability of the cementite layer and distribution of granular ferrite:differential scanning calorimetry(DSC)analysis shows that the sample is accompanied by submicron granular ferrite which is located closer to the surface has higher thermal stability under galvanizing temperature(450°C).A new mechanism of the torsion delamination of pearlitic steel wires is discussed in terms of the thermal stability of the cementite layer and distribution of granular ferrite.