Synthesis and optical properties of novel Gd^(3+)-doped BaZn_(2)(PO_(4))_(2)glass-ceramics for radiation detection applications
Synthesis and optical properties of novel Gd3+-doped BaZn2(PO4)2 glass-ceramics for radiation detection applications作者机构:Key Laboratory of Functional Materials and Devices for Special Environments of CASXinjiang Key Laboratory of Electronic Information Materials and DevicesXinjiang Technical Institute of Physics&Chemistry of CASUrumqi 830011China University of Chinese Academy of SciencesBeijing 100049China Center of Materials Science and Optoelectronics EngineeringUniversity of Chinese Academy of SciencesBeijing 100049China Laboratory of Solid-State Radiation PhysicsUrumqi 830011China
出 版 物:《Journal of Rare Earths》 (稀土学报(英文版))
年 卷 期:2022年第40卷第12期
页 面:1927-1934,I0005页
核心收录:
学科分类:08[工学] 1010[医学-医学技术(可授医学、理学学位)] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 1009[医学-特种医学]
基 金:Project supported by the National Natural Science Foundation of China(11675260)
主 题:Glass-ceramics Photoluminescence Continuous wave-optically stimulated luminescence Thermoluminescence Radiation dosimetry Rare earths
摘 要:45 P_(2)O_(5)-15 BaO-25 ZnO-15 B2O_(3)glasses doped with different concentrations(0 mol%,0.1 mol%,0.25 mol%,0.5 mol%,and 0.75 mol%)of Gd^(3+)were prepared by a melt-quenching method and treated to fabricate glass-ceramics containing BaZn_(2)(PO_(4))_(2)crystals by controllable *** structural,optical,and dosimetric properties were *** spectra indicate that the glasses are composed of[PO_(4)],[BO_(3)],and[BO_(4)]basic structural *** XRD pattern analysis indicates that the samples contain BaZn_(2)(PO_(4))_(2)*** the photoluminesce nce(PL)spectra,two emission bands are observed at 307 and 313 nm due to the^(6)P_(5/2)→^(8)S_(7/2)and^(6)P_(7/2)→^(8)S_(7/2)transitions of Gd^(3+),*** OSL dosimetric properties of glass-ceramics were studied further under beta radiation *** optimal Gd^(3+)doping concentration of 0.5 mol%was *** fading of the OSL signal shows that the CW-OSL signal of Gd^(3+)-doped BaZn_(2)(PO_(4))_(2)glass-ceramics decays by about 58.95%within120 h,and the intensity remains stable *** thermoluminescence(TL)curve has three peaks at 164,240,and 344℃.Minimum detectable dose(MDD)of the 0.5 mol%Gd^(3+)-doped BaZn_(2)(PO_(4))_(2)glass-ceramics was calculated as 0.675 *** samples also exhibit good signal reusability and a broad linear dose-response range(0.3-500 Gy).Results show the excellent dosimetric properties of Gd^(3+)-doped BaZn_(2)(PO_(4))_(2)glass-ceramics and their potential application in radiation dosimetry.