Characteristics of MSWI fly ash during vitrification

作     者：田书磊 王琪 汪群慧 马鸿志 

作者机构：Dept.of Environmental Science and Technology Harbin Institute of Technology Dept.of Environmental Science and EngineeringTsinghua University Chinese Research Academy of Environmental Science Dept.of Environmental Science and TechnologyHarbin Institute of Technology 

出 版 物：《Journal of Harbin Institute of Technology(New Series)》 (哈尔滨工业大学学报（英文版）)

年 卷 期：2009年第16卷第1期

页      面：107-110页

核心收录：

学科分类：083002[工学-环境工程] 0830[工学-环境科学与工程（可授工学、理学、农学学位）] 08[工学] 0905[农学-畜牧学] 09[农学] 0836[工学-生物工程] 090501[农学-动物遗传育种与繁殖] 

基　　金：Sponsored by the Chinese Postdoctoral Fund(Grant No.023205030) National Natural Science Foundation of China(Grant No.20577047) 

主　　题：heavy metal SWI fly ash caching concentration 

摘      要：The vitrification characteristics of municipal solid waste incinerator (MSWI) fly ash were investigated. Effects of temperature on the binding efficiency of heavy metals, the change of chemical compositions and the weight loss of fly ash in the range of 800-1350 ℃ were studied. Toxicity Characteristic Leaching Procedure (TCLP) of the United States was used to analyze the leaching characteristics of heavy metals in fly ash and molten slag. Results indicate that chemical compositions, the weight loss of fly ash and the binding efficiency of heavy metals in fly ash have a tremendous change in the range of 1150-1260 ℃. The percentage of CaO, SiO2 and Al2O3 increases with the increasing temperature, whereas it is contrary for SO3, K2O, Na2O and Cl; especially when the temperature is 1260 ℃, the percentage of these four elements decreases sharply from 43.72% to 0.71%. The weight loss occurs obviously in the range of 1150-1260 ℃. Heavy metals of Pb and Cd are almost vaporized above 1000 ℃. Cr is not volatile and its binding efficiency can reach 100% below 1000 ℃. Results of TCLP indicate that the heavy metal content of molten slag is beyond stipulated limit values.