Effects of Sr^(2+) substitution on the structural, dielectric, and piezoelectric properties of PZT-PMN ceramics

作     者：Arvind Kumar S.K. Mishra 

作者机构：Research and Technology Development Centre Sharda University 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2014年第21卷第2期

页      面：175-180页

核心收录：

学科分类：080801[工学-电机与电器] 0808[工学-电气工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：the financial support by Defence Research and Development Organisation(DRDO) Government of India(No.ERIP/ER/0903830/M/01/1235) 

主　　题：ceramic materials strontium substitution structural properties dielectric properties piezoelectricity 

摘      要：This study described the structural, dielectric, and piezoelectric behavior of Pb1-xSrx[（Zr0.52Ti0.48）0.95（Mn1/3Nb2/3）0.05]O3 ceramics （PSZT-PMN, x=0, 0.025, 0.050, and 0.075）, prepared by a semi-wet route. X-ray diffraction, dielectric, and piezoelectric investigations were carried out to analyze the crystal structure. The relative dielectric constant and dielectric loss were both calculated as the functions of temperature. The room-temperature dielectric constant reaches a maximum for a Sr2＋-modified PZT-PMN ceramic with an x value of 0.050, which corresponds to the morphotropic phase boundary （MPB）. Raman spectroscopy studies also confirm the existence of this MPB for x=0.050. The piezoelectric strain coefficients （d33） value shows a maximum response for this composition. In addition, the phase transition temperature decreases significantly when the Sr2＋concentration increases in the PZT-PMN ceramics.