Dielectric properties of bismuth-containing pyrochlores:A comparative analysis
作者机构:Research Institute of Physics Southern Federal Universityav.Stachki 193 Rostov-on-Don344090Russia Research Institute of Solid State Electronics Materials MIREA-Russian Technological University(RTU MIREA)5th Street of Sokolinaya Gora 22 Moscow119454Russia Technological Department Platov South-Russian State Polytechnic University(NPI)Prosvescheniya Str.132Novocherkassk 346428Russia
出 版 物:《Journal of Advanced Dielectrics》 (先进电介质学报(英文))
年 卷 期:2022年第12卷第2期
页 面:29-35页
学科分类:080801[工学-电机与电器] 0808[工学-电气工程] 0809[工学-电子科学与技术(可授工学、理学学位)] 0817[工学-化学工程与技术] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0702[理学-物理学]
基 金:The authors are grateful to L.A.Shilkina for X-ray phase analysis of the BZN samples.The reported study was funded by Russian Science Foundation(RSF)-research projects no.20-72-00086(BZN ceramics preparation,dielectric mea-surements) At RTU MIREA,the work was supported by the Ministry of Science and Higher Education of Russia(project FSFZ 0706-2020-2022,Bi2Ti2O7 single crystal growth),the equipment of the Center for Collective Use of RTU MIREA was used
主 题:Pyrochlores relaxor behavior bismuth titanate dielectric permittivity geometric frustration
摘 要:The comparative analysis of the dielectric properties of bismuth-containing pyrochlores with different manifestation of atomic order/disorder was carried *** examined the dielectric properties(including behavior in electric fields)of two pyrochlore compounds:BZN(presumably a composition close to Bi_(1.5)Zn_(0.5)Nb_(1.5)O_(6.5))ceramics with chemical disorder in both A and B cation sublattices and Bi_(2)Ti_(2)O_(7)single crystal with fully chemical ordered *** fundamental differences between the dielectric properties of the BZN ceramics and Bi_(2)Ti_(2)O_(7)single crystal were *** particular,in the dielectric relaxation behavior(which cannot be described via Arrhenius law in the Bi_(2)Ti_(2)O_(7))or in the influence of the electric fields on the dielectric permittivity(split-ting of the field-cooled and zero-field-cooled behaviors was observed for Bi_(2)Ti_(2)O_(7)below estimated freezing temperature).The results of this study highlights the special role of Bi_(2)Ti_(2)O_(7)as a candidate material for studying aspects of geometric frustration related with pyrochlore structure in non-magnetic medium and specifies the future directions of research.