Corrosion resistance and antibacterial activity of different zones in TA2 weldment by TIG welding

作     者：Yan-Ping Zhu Chang-Yi Li Lian-Yun Zhang Yan-Ping Zhu;Chang-Yi Li;Lian-Yun Zhang

作者机构：Department of ProsthodonticsTianjin Stomatological HospitalTianjin300041China School of StomatologyTianjin Medical UniversityTianjin300070China 

出 版 物：《Rare Metals》 (稀有金属（英文版）)

年 卷 期：2020年第39卷第12期

页      面：1449-1456页

核心收录：

学科分类：08[工学] 0806[工学-冶金工程] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：the National Natural Science Foundation of China(No.81070871)。 

主　　题：Titanium Tungsten inert gas welding Corrosion resistance Artificial saliva solution Antibacterial activity 

摘      要：The corrosion resistance behavior of TA2 pure titanium processed by tungsten inert gas(TIG)welding was investigated in artificial saliva solution at 37℃.By metallographic examination,electrochemical measurement technology,and electrochemical impedance spectroscopy(EIS),the corrosion resistance of the base metal(BM),heat-affected zone(HAZ),and weld metal(WM)were investigated.Metallographic examination experiments show that welding process would cause the growth of grain size.In addition,phase change happens in the HAZ and WM.The change of grain size and phase would influence the generation of the original passive film.The electrochemical tests show that the BM,HAZ,and WM are all equipped with good corrosion resistance.The welded joint shows a better corrosion resistance than the original TA2.It is shown that the BM with the lowest corrosion potential and the biggest corrosion current has a worse corrosion resistance than WM as well as HAZ.Silver(Ag)nanoparticles can be distributed on the WM zone of Ti uniformly.The WM zone of Ti with Ag coating considerably enhances the antibacterial activity of Ti implants.