Effect of Universal Primers on the Tensile Bond Strength between Zirconia and Resin Composites

作     者：Akinori Ohno Mizuki Nagata Hiroaki Kobayashi Hiroaki Yamaguchi Katsura Ohashi Kaori Aoki Tomotaro Nihei Katsuhiko Kimoto 

作者机构：Department of Oral Interdisciplinary Medicine Prosthodontics&Oral ImplantologyGraduate School of DentistryKanagawa Dental University82 Inaoka-choYokosukaKanagawa 238-8580Japan Division of Clinical BiomaterialsDepartment of Oral ScienceGraduate School of DentistryKanagawa Dental University82 Inaoka-choYokosukaKanagawa 238-8580Japan 

出 版 物：《材料科学与工程（中英文B版）》 (Journal of Materials Science and Engineering B)

年 卷 期：2021年第11卷第1期

页      面：1-7页

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：Universal primer zirconia composite resin bond strength. 

摘      要：This study aimed to evaluate the effects of universal primers on the tensile bond strength between zirconia and resin *** specimens were divided into five groups based on the surface treatment with the following primers:MP(Monobond Plus),SU(ScotchBond Universal),AZ(AZ Primer),BM(Beauty bond Multi),and BL(Bondmer Lightless).After priming,stainless steel rods were bonded to the zirconia specimens with composite *** tensile bond strength test was performed:stored at room temperature for 1 day;stored in distilled water at 37°C for 7 days;and underwent thermal *** BL group demonstrated a significantly higher tensile bond strength than other groups when stored at room temperature for 1 day(p0.05).The primer that acted via chemical polymerization appeared to be most effective in improving the bond strength between the two materials in this study.