Microstructural characterization of blanked surface of C5191 phosphor bronze sheet under ultra-high-speed blanking
C5191磷青铜薄板超高速冲裁断面的显微组织特征作者机构:Engineering Technology Training CenterNanjing Vocational University of Industry TechnologyNanjing 210023China Jiangsu Key Laboratory of Precision and Micro-Manufacturing TechnologyNanjing University of Aeronautics and AstronauticsNanjing 210016China School of Mechanical EngineeringNanjing Vocational University of Industry TechnologyNanjing 210023China
出 版 物:《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报(英文版))
年 卷 期:2021年第31卷第3期
页 面:692-702页
核心收录:
学科分类:0806[工学-冶金工程] 08[工学] 0818[工学-地质资源与地质工程] 0815[工学-水利工程] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0813[工学-建筑学] 0703[理学-化学] 0814[工学-土木工程] 0702[理学-物理学]
基 金:The authors are grateful for the financial supports from Jiangsu Key Laboratory of Precision and Micro-manufacturing Technology of China(JSJMYWX2020-01) Zhejiang Provincial Natural Science Foundation of China(LY18E050005) the Startup Foundation for Introducing Talent of Nanjing Institute of Industry Technology(YK18-13-02)of China
主 题:C5191 phosphor bronze ultra-high-speed blanking blanked surface adiabatic shear dynamic recrystallization
摘 要:The deformation mechanism of C5191 phosphor bronze sheet under ultra-high-speed blanking was *** virtue of a DOBBY-OMEGA F1 ultra-high-speed press,the ultra-high-speed blanking test was conducted on C5191 phosphor bronze sheets with a thickness of 0.12 mm at 3000 strokes per *** microstructures of the blanked edges were characterized and analyzed separately by electron back-scatter diffraction(EBSD)and transmission electron microscopy(TEM).The results show that grains in the blanked edges are stretched along the blanking ***{001}cube textures(maximum pole densities of 9 and 12,respectively)and secondarily strong{011}textures(maximum pole densities of 4 and 7,respectively)are formed in local ***,deformation twins are found in the shear zone of the blanked edges which are rotated and coarsened due to the blanking-induced extrusion and local thermal effect which can further form into sub-grains with clear and high-angle *** C5191 phosphor bronze sheet is subjected to adiabatic shear during ultra-high-speed blanking,accompanied with dynamic recrystallization.