Synthesis and properties of nickel borate acylate as a new rubber-steel cord adhesion promoter

作     者：LI Xiao ru 1,NIE Xi du 2,WU Hai ying 1,CHENG Ben cheng 1 (1 College of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China 2 Hengyang Branch of Hunan University, Hengyang 412000, China) 

作者机构：College of Chemistry and Chemical Engineering Central South University Changsha China Hengyang Branch of Hunan University Hengyang China 

出 版 物：《Journal of Central South University of Technology》 (中南工业大学学报（英文版）)

年 卷 期：2001年第8卷第4期

页      面：244-248页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0802[工学-机械工程] 0801[工学-力学（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：ScienceFundofScienceandTechnologyCommissionofHunanProvince(No .0 1 96 2 5 0 2 ) 

主　　题：nickel borate acylate adhesion promoter nickel carbonate borate 

摘      要：The synthetic method of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. The preparation of nickel carbonate could be performed through reaction of nickel sulfate with sodium carbonate in aqueous solution, in which fractional conversion of nickel was more than 99.9%. The mixed nickel carboxylate was prepared by the reaction of nickel carbonate with isooctanoic acid and acetic acid, under strong stirring for 2 h, the mole ratio of these chemicals were 1∶1∶1.1 respectively, and water should be removed completely by adding of inert organic solvent after reaction was finished so as to avoid hydrolysis of tributyl borate in the second reaction. NBA was synthesized by reaction of mixed nickel carboxylate with tributyl borate under strong stirring at 200 250 ℃ for 6 h. By detection and comparison with 680C product from Manobond Company of England, the NBA synthesized through isooctanoic acid and tributyl borate was very similar to product 680C in IR data, 300% fixed extension strength, tensile strength, hardness and cure curve, and was slightly lower than those of product 680C in tensile failure extensibility and hot air aging. The experimental results show that the prepared NBA can be used as rubber steel cord AP.