Effect of Cu content on microstructure and mechanical properties of in-situ β phases reinforced Ti/Zr-based bulk metallic glass matrix composite by selective laser melting(SLM)

作     者：Xuehao Gao Xin Lin Qiaodan Yan Zihong Wang Xiaobin Yu Yinghui Zhou Yunlong Hu Weidong Huang Xuehao Gao;Xin Lin;Qiaodan Yan;Zihong Wang;Xiaobin Yu;Yinghui Zhou;Yunlong Hu;Weidong Huang

作者机构：State Key Laboratory of Solidification ProcessingNorthwestern Polytechnical UniversityXi’an710072China Key Laboratory of Metal High Performance Additive Manufacturing and Innovative DesignMUT ChinaNorthwestern Polytechnical UniversityXi'an710072China 

出 版 物：《Journal of Materials Science & Technology》 (材料科学技术（英文版）)

年 卷 期：2021年第67卷第8期

页      面：174-185页

核心收录：

学科分类：0806[工学-冶金工程] 0817[工学-化学工程与技术] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0703[理学-化学] 0802[工学-机械工程] 0702[理学-物理学] 0801[工学-力学（可授工学、理学学位）] 

基　　金：supported by the National Key Research and Development Plan of China(No.2018YFB0704101) the Fundamental Research Funds for the Central Universities(No.3102019ZX013) the Planning Programme of Shan Xi Province’s Co-Ordination and Innovation Project of Science and Technology(No.2016KTZDCY02-02) 

主　　题：Metallic glass Amorphous phase βPhase Bulk metallic glass matrix composites(BMGCs) Additive manufacturing(AM) Selective laser melting(SLM) 

摘      要：In this study,non-toxic in-situβphases of reinforced Ti/Zr-based bulk metallic glass matrix composites(BMGCs)of(Ti_(0.65)Zr_(0.35))100-xCux(x=5,10,15 at.%)are fabricated via selective laser *** effect of Cu content on phase formation,microstructure,and mechanical properties is *** average volume fraction and width of theβphase decreases with increasing Cu content,while a more amorphous phase and the(Ti,Zr)_(2)Cu phase *** the center zone of the molten pool,theβphase grows in the direction of the temperature gradient,and the amorphous phase distributes among theβ*** occurs using:sphere morphology(for x=5),a more continuous elongated sphere and network morphology(for x=10),and network morphology(for x=15),*** the edge zone of the molten pool,due to the smaller cooling rate and the existence of a partially molten zone,theβphase becomes coarser,and an amorphous phase forms for more continuous ***,the hardness improves significantly with increasing Cu *** crack is found for x=*** the average volume fraction of theβphase for x=5 is about 90%,the compression yield strength is 1386±64 MPa,reaching to an average level of conventionally fabricated counterparts,due to finer microstructure,and twinning and martensitic transformation of theβphase.