Developing Core-Shell Nano-Structures in FeCrAl-ODS Ferritic Alloys with the Co-Addition of Ni and Zr

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 2024年第2期37卷 364-372页

作者： Wenquan Ding Jieli Ma Yong Jiang Yiren Wang Huiqun Liu key laboratory for nonferrous materials of Ministry of Education School of Materials Science and EngineeringCentral South UniversityChangsha410083China National key laboratory for Powder Metallurgy Central South UniversityChangsha410083China

A new Ni+Zr co-alloyed FeCrAl-ODS(oxide-dispersion-strengthened)ferritic alloy was fabricated by ball-milling and hot-isostatic-pressing.Using electron microscopy and atom probe tomography,the dispersive formation of high density core-shelled nano-particles of various sizes was confirmed with a common B2-NiAl shell.Among which,median-sized nano-particles(20-50 nm)typically have an Y_(4)Al_(2)O_(9)nano-core of<~20 nm,ultra-fine nano-particles(<~20)nm have an Y_(4)Zr_(3)O_(12)nano-core of<~10 nm,and larger-sized nano-particles(50-100 nm)incorporate an ultra-fine Y_(4)Al_(2)O_(9)nano-core and a few ultra-fine Y_(4)Zr_(3)O_(12)nano-oxides.All these nano-phases were highly coherent with the ferritic matrix.No large Y--Al-O nano-oxides were formed.The total number density of ultra-fine nano-particles was estimated as~2×10^(23)m^(-3)with a mean size of 6.3 nm only,and accordingly,the new alloy achieved an excellent combination of strength and ductility at high temperatures.

关键词： FeCrAl Oxide-dispersion-strengthened(ODS)alloy Mechanical alloying Nano-oxides Core-shell

Negative enthalpy alloys and local chemical ordering:a concept and route leading to synergy of strength and ductility

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

National science Review 2024年第4期11卷 172-184页

作者： Zibing An Tao Yang Caijuan Shi Shengcheng Mao Lihua Wang Ang Li Wei Li Xianmeng Xue Ming Sun Yifan Bai Yapeng He Fuzeng Ren Zhouguang Lu Ming Yan Yang Ren Chain-Tsuan Liu Ze Zhang Xiaodong Han Beijing key Lab of Microstructure and Property of Advanced materials College of Materials Science &Engineering Beijing University of Technology Department of materials science and engineering City University of Hong Kong key laboratory of Partial Acceleration Physics& Technology Institute of High Energy PhysicsChinese Academy of Sciences Department of materials science &engineering Southern University of Science and Technology Department of Physics City University of Hong Kong State key laboratory of Silicon materials Department of Materials Science and Engineering Zhejiang University

Solid solutions are ubiquitous in metals and alloys. Local chemical ordering(LCO) is a fundamental sub-nano/nanoscale process that occurs in many solid solutions and can be used as a microstructure to optimize strength and ductility. However, the formation of LCO has not been fully elucidated, let alone how to provide efficient routes for designing LCO to achieve synergistic effects on both superb strength and ductility. Herein, we propose the formation and control of LCO in negative enthalpy alloys. With engineering negative enthalpy in solid solutions, genetic LCO components are formed in negative enthalpy refractory high-entropy alloys(RHEAs). In contrast to conventional ‘trial-and-error' approaches, the control of LCO by using engineering negative enthalpy in RHEAs is instructive and results in superior strength(1160 MPa) and uniform ductility(24.5%) under tension at ambient temperature, which are among the best reported so far. LCO can promote dislocation cross-slip, enhancing the interaction between dislocations and their accumulation at large tensile strains; sustainable strain hardening can thereby be attained to ensure high ductility of the alloy. This work paves the way for new research fields on negative enthalpy solid solutions and alloys for the synergy of strength and ductility as well as new functions.

关键词： negative enthalpy alloys local chemical ordering strength ductility dislocation

Micelle-directed self-assembly of single-crystal-like mesoporous stoichiometric oxides for high-performance lithium storage

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

National science Review 2024年第4期11卷 195-205页

作者： Yanhua Wan Changyao Wang Xingmiao Zhang Yang Yin Mengmeng Liu Bing Ma Linlin Duan Yuzhu Ma Wei Zhang Changlin Zheng Dongliang Chao Fei Wang Yongyao Xia Wei Li Department of Chemistry Laboratory of Advanced Materials Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials State Key Laboratory of Molecular Engineering of Polymers College of Chemistry and Materials ScienceFudan University State key laboratory of Surface Physics and Department of Physics Fudan University

Due to their uncontrollable assembly and crystallization process,the synthesis of mesoporous metal oxide single crystals remains a formidable challenge.Herein,we report the synthesis of single-crystal-like mesoporous Li2TiSiO5by using soft micelles as templates.The key lies in the atomic-scale self-assembly and step-crystallization processes,which ensure the formation of single-crystal-like mesoporous Li2TiSiO5microparticles via an oriented attachment growth mechanism under the confinement of an in-situ formed carbon matrix.The mesoporous Li2TiSiO5anode achieves a superior rate capability(148 mAh g-1at5.0 A g-1) and outstanding long-term cycling stability(138 mAh g-1after 3000 cycles at 2.0 A g-1) for lithium storage as a result of the ultrafast Li+diffusion caused by penetrating mesochannels and nanosized crystal frameworks（5-10 nm）.In comparison,bulk Li2TiSiO5exhibits poor rate capability and cycle performance due to micron-scale diffusion lengths.This method is very simple and reproducible,heralding a new way of designing and synthesizing mesoporous single crystals with controllable frameworks and chemical functionalities.

关键词： mesoporous materials micelles single-crystal-like Li2TiSiO5 lithium-ion batteries

Surface reconstruction of heterostructures in alkaline medium towards enhanced electrocatalytic hydrogen evolution

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Rare Metals 2024年第6期43卷 2636-2647页

作者： Ming-Yang Yang Ji Yuan Xue-Lian Fu Jing-Jing Chen Jing Hu Zhou-Guang Lu Chen Liu Guangdong Research Center for Interfacial engineering of Functional materials Shenzhen Key Laboratory of Polymer Science and TechnologyShenzhen Key Laboratory of Energy Electrocatalytic MaterialsCollege of Materials Science and EngineeringShenzhen University Shenzhen key laboratory of Interfacial science and engineering of materials Department of Materials Science and EngineeringSouthern University of Science and Technology

Constructing heterostructures has proved to be a successful strategy to fabricate electrocatalysts with high efficiency for water splitting.However,the structure evolution in alkaline hydrogen evolution reaction lacks investigation and the specific active center remains disputable.Herein,we take the well-designed Ni3S2@VO2heterostructures as a model to investigate the electrocatalytic activity and the surface reconstruction process of heterostructure catalysts in alkaline electrolyte.The Ni3S2@VO2heterostructures,with Ni3S2nanorods as the core and VO2nanoflakes as the shell,coupled with the high conductive Ni3S2,the hydrophilic VO2and modulated electronic structures at the interfaces,exhibited prominent activity and superior stability at various current densities.Further,the ex-situ characterizations confirmed that the surface reconstruction from Ni3S2@VO2into Ni3S2@amorphous-Ni（OH）2in alkaline media could optimize the water dissociation barrier and exposed large active area,thereby contributing to improved electrocatalytic performance.Our study not only introduces novel high-performance electrocatalysts for hydrogen evolution reaction（HER）,but also provides a new avenue for re-examining hetero-structural catalysts in alkaline solutions.

关键词： Heterostructures Ni 3 S 2 @VO 2 Surface reconstruction Water dissociation Alkaline hydrogen evolution

Crystalline-amorphous M@MNx（M=Co,Fe,Ni）encapsulated in nitrogen-doped carbon for enhanced efficient and durable hydrogen evolution reaction

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Rare Metals 2024年第4期43卷 1547-1556页

作者： Yang Yang Xiao-Chuan Duan Shao-Hui Guo Xian-Ming Zhang College of materials science and engineering College of ChemistryKey Laboratory of Interface Science and Engineering in Advanced MaterialsTaiyuan University of Technology

Developing earth-abundant electrocatalysts for hydrogen evolution reaction（HER） is important for the sustainable energy economy.Herein,efficient and stable heterocatalysts consisting of crystalline-amorphous M@MNx（M=Co,Fe,Ni） encapsulated in N-doped carbon layers supported with N-doped graphene sheets（denoted as M@MNx@NC-NG） are synthesized by facile hydrothermal reaction and nitridation process.During the nitriding process,metal ions in M（tzbc）2（H2O）4(tzbc=4-（1H-1,2,4-triazol-1-yl） benzoic acid) complexes are reduced to crystalline M cores,accompanied by the formation of amorphous MNxshells;the tzbc ligands are insitu carbonized to form outermost N-doped carbon（NC）layers that connect with inner MNxvia M-N-C motifs inherited from the complex precursors and inhibit the transition of MNxfrom amorphous to crystalline phase.The Co@CoNx@NC-NG catalyst exhibits excellent HER activity with small overpotentials of 45 and 64 mV at a cathode current density of 10 mA·cm-2and low Tafel slopes of 40 and 85 mV·dec-1in 0.5 mol·L-1H2SO4and1.0 mol·L-1KOH electrolytes,respectively.The Co@CoNx@NC-NG retains 97% of the initial overpotential after 100,000 s in both acidic and alkaline media.Such outstanding HER performance originates from the crystalline-amorphous Co@CoNxthat redistributes electrons around the heterointerfaces,facilitating the conversion process of H+/H2O to hydrogen and thereby promoting HER kinetics.The outermost NC layers serve as the armor of Co@CoNx,and graphene nanosheets act as carriers of egg-like Co@CoNx@NC and conduction paths for electron shuttles,ensuring stable and continuous electrocatalytic hydrogen production.

关键词： Hydrogen evolution reaction Electrocatalysts Iron group metals Heterojunction Crystalline-amorphous structure

Long-wave infrared emission properties of strain-balanced InAs/InxGa1-xAsySb1-y type-Ⅱ superlattice on different substrates

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Rare Metals 2024年第7期43卷 3194-3204页

作者： Chao Shi Xuan Fang Hong-Bin Zhao Deng-Kui Wang Xi Chen Dan Fang Dong-Bo Wang Xiao-Hua Wang Jin-Hua Li State key laboratory of High Power Semiconductor Lasers School of PhysicsChangchun University of Science and Technology State key laboratory of Advanced materials for Smart Sensing China General Research Institute for Nonferrous Metals Department of Opto-Electronic Information science School of Materials Science and EngineeringHarbin Institute of Technology

High-performance type-Ⅱ superlattices of Ⅲ-Ⅴsemiconductor materials play an important role in the development and application of infrared optoelectronic devices.Improving the quality of epitaxial materials and clarifying the luminescent mechanism are of great significance for practic al applic ations.In this work,strain-balanced and high-quality In As/InxGa1-xAsySb1-ysuperlattices without lattice mismatch were achieved on InAs and GaSb substrates successfully.Superlattices grown on In As substrate could exhibit higher crystal quality and surface flatness based on high-resolution X-ray diffraction（HRXRD） and atomic force microscopy（AFM） measurements' results.Moreover,the strain distribution phenomenon from geometric phase analysis indicates that fluctuations of alloy compositions in superlattices on GaSb substrate are more obvious.In addition,the optical properties of superlattices grown on different substrates are discussed systematically.Because of the difference in fluctuations of element composition and interface roughness of superlattices on different substrates,the superlattices grown on In As substrate would have higher integral intensity and narrower full-width at half maximum of long-wave infrared emission.Finally,the thermal quenching of emission intensity indicates that the superlattices grown on the In As substrate have better recombination ability,which is beneficial for increasing the operating temperature of infrared optoelectronic devices based on this type of superlattices.

关键词： Photoluminescence Alloy compositions fluctuations InAs(Sb)/In x Ga 1− x As y Sb 1− y Type-II superlattice Substrate

Effect of Ga on the microstructure and properties of NiCoV alloy at different annealing temperatures

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Progress in Natural science:materials International 2024年第2期34卷 408-419页

作者： Jin Li Peng Wang Lvxing Chen Meifeng He Jun Cheng School of materials and Chemistry University of Shanghai for Science and Technology Northwest Institute for nonferrous Metal Research Shaanxi Key Laboratory of Biomedical Metal Materials

To obtain a high-entropy alloy characterized by high strength and plasticity,（NiCoV）100-xGaxx=0,5,7) was successfully prepared,cold-rolled,and heat-treated.The microstructure was analyzed to correlate Ga content with the performance of the system.The addition of Ga can produce alloying effects,including solid solution strengthening effect,second phase precipitation strengthening effect,and layer misalignment energy reduction effect.The experimental results show adding Ga elements can enrich Ni,Co,V,and Ga above the grain boundaries,causing the alloy to produce annealed twins inside.The alloy is strengthened mainly by precipitation,and the formation of the precipitation phase effectively enhances the strength of the alloy.The low stacking fault energy promotes the toughening of NiCoV but makes the plasticity of the alloy decrease.Still,the formation of annealed twins effectively increases the plasticity,which makes the alloy harder but does not reduce the plasticity too much.By comparing the experimental properties,（NiCoV）93Ga7showed the best mechanical properties at the annealing temperature of 900℃,yield strength,tensile strength and elongation of 906 MPa,1321 MPa and21.36 %,respectively.

关键词： Annealing treatment High entropy alloy Mechanical properties Precipitation strengthening Twin strengthening

Rheological Behaviors of Polymers with Nanoparticles Tethered at Each End

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Chinese Journal of Polymer science 2024年第3期42卷 400-406,I0009页

作者： Song-Qi Zhang Wen-Qing Wang Jia-Ping Lin Li-Quan Wang Shanghai key laboratory of Advanced Polymeric materials Key Laboratory for Ultrafine Materials of Ministry of EducationSchool of Materials Science and EngineeringEast China University of Science and TechnologyShanghai 200237China

The polymer with nanoparticles tethered at each end is a unique model for unraveling the effect of chain ends on the polymer dynamics. We investigated the rheological behavior of this kind of polymer by using nonequilibrium molecular dynamics simulation. The effect of polymer lengths and nanoparticle radii on the complex moduli and viscosity was examined. The dependence of complex moduli on the frequency becomes less pronounced as the polymer is short or the nanoparticle is large. The shear thinning behavior was revealed for these systems, and the scaling exponent of complex viscosity with respect to the frequency was found to change from-1/2 to-3/4 as the polymer shortens or the nanoparticle enlarges. The rheological behavior was further explained by analyzing the mean square distance of nanoparticles. The simulation results were compared with the existing experimental finding, showing an agreement. The work provides information for understanding the chain end effect on polymer rheology.

关键词： Polymer rheology Modulus Viscosity Molecular dynamics

维普期刊数据库

Ultrafast micro/nano-manufacturing of metastable materials for energy

在线全文

学校读者我要写书评

暂无评论

National science Review 2024年第4期11卷 283-298页

作者： Xiaoya Cui Yanchang Liu Yanan Chen School of materials science and engineering Key Laboratory of Advanced Ceramics and Machining Technology(Ministry of Education) and Tianjin Key Laboratory of Composite and Functional MaterialsTianjin University Ministry of Education key laboratory of Protein sciences School of Life SciencesTsinghua University

The structural engineering of metastable nanomaterials with abundant defects has attracted much attention in energy-related fields. The high-temperature shock(HTS) technique, as a rapidly developing and advanced synthesis strategy, offers significant potential for the rational design and fabrication of high-quality nanocatalysts in an ultrafast, scalable, controllable and eco-friendly way. In this review, we provide an overview of various metastable micro-and nanomaterials synthesized via HTS, including single metallic and bimetallic nanostructures, high entropy alloys, metal compounds(e.g. metal oxides) and carbon nanomaterials. Note that HTS provides a new research dimension for nanostructures, i.e. kinetic modulation. Furthermore, we summarize the application of HTS—as supporting films for transmission electron microscopy grids—in the structural engineering of 2D materials, which is vital for the direct imaging of metastable materials. Finally, we discuss the potential future applications of high-throughput and liquid-phase HTS strategies for non-equilibrium micro/nano-manufacturing beyond energy-related fields.It is believed that this emerging research field will bring new opportunities to the development of nanoscience and nanotechnology in both fundamental and practical aspects.

关键词： high-temperature shock technique defect engineering metastable phase kinetic modulation non-equilibrium micro/nano-manufacturing