Particuology 2024年第5期88卷 116-127页

作者： Zhilong Wang Zhenzhen Zhao Ye Yang An Zhang Xiayi Liu Tong Zhao Yahui Cui School of Mechanical and Precision instrument engineering Xi'an University of TechnologyXi'an 710048China

This paper presents the effects of both poly vinylidene fluoride(PVDF)/carbon black(CB)ratio(m PVDF:m CB)and mixing time t on the dispersion mechanism of the cathode slurry of lithium-ion battery(LIB).The dispersion mechanism is deduced from the electrochemical,morphological and rheological properties of the cathode slurry by using electrical impedance spectroscopy(EIS),scanning electron microscopy and rheology methods,*** the perspective of EIS method,static simulation models are established in the COMSOL Multiphysics software;meanwhile,the simulated results are used to verify the correctness of the electrochemical properties of the cathode *** a result,the following conclusions are able to be ***,in the case of the mass ratio m_(PVDF):m_(CB)=5:10,LiCoO_(2) particles are completely coated by the mixture of CB and PVDF to form a stable polymer gel *** or lower m_(PVDF):m_(CB) leads to the larger impedance and worse dispersion status for the cathode ***,when t=6 min,a good gel-like conductive network structure is formed by coating the thinner evenly dispersed CB–PVDF double layer around LiCoO_(2) ***,a strategy regarding to both m_(PVDF):m_(CB) and t in experimental scale is proposed,which has the capability of improving the performance of LIB.

关键词： Cathode slurry Dispersion mechanism Lithium-ion battery(LIB)

Optimization of mixing speed and time to disperse the composite conductive agent composed of carbon black and graphene in lithium-ion battery slurry

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Particuology 2024年第9期92卷 1-12页

作者： Zhilong Wang Jialong Tu Xinhao Yu Feixiang Li Zhenzhen Zhao Yahui Cui Tong Zhao Faculty of Mechanical and Precision instrument engineering Xi'an University of TechnologyXi'an710048China

This paper proposed an optimal approach to disperse the composite conductive agent which is composed of carbon black(CB)and graphene(Gr)within lithium-ion battery(LIB)slurry with different mixing speeds and mixing *** internal structures of LIB slurry are characterized by Electrochemical Impedance Spectroscopy,Scanning Electron Microscopy,and Raman ***,a composite conductive solution is prepared by mixing the composite conductive agent with NMP solvent under the conditions of five different mixing speeds n_(1)(n_(1)=1000,1100,1200,1300,1400 rpm)in the case of mixing time t_(1)=10 ***,LIB slurry is prepared by blending the composite conductive solution,LiCoO_(2)and PVDF-NMP solution under the conditions of five different mixing speeds n_(2)(n_(2)=1000±280,1100±280,1200±280,1300±280,1400±280 rpm)in the case of mixing time t_(2)=6 *** analyzing the internal structure of different LIB slurries,it shows that in the case of n_(1)=n_(2)=1200 rpm,a conductive network structure is well formed within LIB ***,in order to determine the optimal time to prepare the composite conductive solution for LIB slurry,nine different t_(1)(t_(1)=0,10,20,30,40,50,60,70,80 min)are *** analyzing the internal structure of different LIB slurries,a well-formed conductive network structure and a uniformly distributed composite conductive agent are deduced in LIB slurry when t_(1)=50 ***,it can be concluded that the composite conductive agent composed of CB and Gr is able to be uniformly dispersed in LIB slurry by establishing a well-formed conductive network structure under the optimal mixing speed n_(1)=n_(2)=1200 rpm and the optimal mixing time t_(1)=50 min,t_(2)=6 *** kind of the internal structure has the potential to be used to further analyze the dispersion characterizations of LIB slurry under different composite conductive agent and CB/Gr ratios with the aim of improving the final performance of LIB.

关键词： Lithium-ion battery slurry Composite conductive agent Carbon black Graphene

3D nano-printed geometric phase metasurfaces for generating accelerating beams with complex amplitude manipulation

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Science China(Physics,Mechanics & Astronomy) 2024年第6期67卷 86-95页

作者： Tianchen Tang Saima Kanwal Yongzheng Lu Yuelong Li Shuangbao Wu Lei Chen Ziheng Qian Zhouyu Xie Jing Wen Dawei Zhang research center of Optical instrument and System Ministry of Education and Shanghai Key Lab of Modern Optical SystemUniversity of Shanghai for Science and TechnologyShanghai 200093China

Metasurface,a forefront in emerging optical devices,has demonstrated remarkable potential for complex amplitude manipulation of light ***,prevailing approaches face challenges in spatial resolution and complexities associated with integrating dynamic phases,impeding the simplified design and reproducible fabrication of ***,we introduce an innovative approach for complex amplitude modulation within 3D nano-printed geometric phase *** approach enables the generation of self-accelerating beams by encoding amplitude through phase-only manipulation,achieving high spatial ***,this method circumvents the conventional need to adjust the geometric parameters of metasurface unit structures for amplitude manipulation,offering a streamlined and efficient route for design and fabrication *** novel methodology holds promise for expedited and low-cost manufacturing of complex amplitude manipulation metasurfaces.

关键词： metasurface complex amplitude manipulation geometric phase 3D nano-printing Airy beam accelerating parabolic beam

High adsorption selectivity of activated carbon and carbon molecular sieve boosting CO_(2)/N_(2) and CH_(4)/N_(2) separation

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Chemical engineering 2024年第3期67卷 282-297页

作者： Siang Chen Wenling Wu Zhaoyang Niu Deqi Kong Wenbin Li Zhongli Tang Donghui Zhang The research center of Chemical engineering School of Chemical Engineering and TechnologyTianjin UniversityTianjin 300072China

Flue gas and coal bed methane are two important sources of greenhouse *** swing adsorption process has a wide range of application in the field of gas separation,and the selection of adsorbent is *** this regard,in order to assess the better adsorbent for separating CO_(2) from flue gas and CH_(4) from coal bed methane,adsorption isotherms of CO_(2),CH_(4) and N_(2) on activated carbon and carbon molecular sieve are measured at 303.15,318.15 and 333.15 K,and up to 250 *** experimental data fit better with Langmuir 2 compared to Langmuir 3 and Langmuir-Freundlich models,and Clausius-Clapeyron equation was used to calculate the isosteric *** the order of the adsorbed amount and the adsorption heat on the two adsorbents are CO_(2)>CH_(4)>N_(2).The adsorption kinetics are calculated by the pseudo-first kinetic model,and the order of adsorption rates on activated carbon is N_(2)-CH_(4)>CO_(2),while on carbon molecular sieve,it is CO_(2)-N_(2)>CH_(4).It is shown that relative molecular mass and adsorption heat are the primary effect on kinetics for activated carbon,while kinetic diameter is the main resistance factor for carbon molecular ***,the adsorption selectivity of CH_(4)/N_(2) and CO_(2)/N_(2) were estimated with the ideal adsorption solution theory,and carbon molecular sieve performed best at 318.15 K for both CO_(2) and CH_(4) *** study suggested that activated carbon is a better choice for separating flue gas and carbon molecular sieve can be a strong candidate for separating coal bed methane.

关键词： Activated carbon Carbon molecular sieve Adsorbent evaluation Adsorption equilibrium and kinetics Heat of adsorption Selectivity

Compositional tuning of A2B7-type La0.7-xYxMg0.3Ni3.5 alloys for gaseous hydrogen storage

在线全文

学校读者我要写书评

暂无评论

Journal of Rare Earths 2024年第10期42卷 1912-1919页

作者： Junkun Du Hui Wang Renheng Tang Jiangwen Liu Liuzhang Ouyang Min Zhu School of Materials Science and engineering Guangdong Engineering Technology Research Center of Advanced Energy Storage MaterialsSouth China University of Technology

Rare earth-based superlattice alloys have great potential for gaseous hydrogen storage,as well as successful application as nickel-metal hydride batteries *** this work,Y substitution was carried out to adjust the gaseous hydrogen storage properties of A2B7-type *** results indicate a multiphase structure in the alloys comprised of the main rhombohedral Gd2Co7and PuNi3phases,with a small amount of ***,the Y substitution results in higher abundance of the *** alloy La0.42Y0.28Mg0.3Ni3.5exhibits a hydrogen storage cap acity of 1.55 wt% at 298 K and a desorption plateau pressure of 0.244 *** addition,this alloy demonstrates a stable cycle life by a capacity retention of 94.2% after 50 cycles,with the main capacity degradation occurring during the initial 20 *** work accentuates the potential of the La-Y-Mg-Ni-based superlattice alloys for applications in solid-state hydrogen storage.

关键词： A2B7-type La–Mg–Ni alloys Cycle performance Desorption plateau pressure Hydrogen storage Rare earths Y substitution

Enrichment of anammox biomass during mainstream wastewater treatment driven by achievement of partial denitrification through the addition of bio-carriers

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Journal of Environmental Sciences 2024年第3期137卷 181-194页

作者： Yuqing Ma Bo Wang Xiaodi Li Shuo Wang Wen Wang Yongzhen Peng National engineering Laboratory for Advanced Municipal Wastewater Treatment and Reuse technology Engineering Research Center of BeijingBeijing University of TechnologyBeijing 100124China

Anammox is widely considered as the most cost-effective and sustainable process for nitrogen ***,how to achieve the enrichment of anammox biomass remains a challenge for its large-scale application,especially in mainstream wastewater *** this study,the feasibility of enrichment of anammox biomass was explored through the realization of partial denitrification and the addition of *** using ordinary activated sludge,a sequencing batch reactor(SBR)followed by an up-fow anaerobic sludge bed(UASB)was operated at 25±2℃ for 214 *** long-term operation was divided into five phases,in which SBR and UASB were started-up in Phases I and II,*** eliminating oxygen and adjusting the infow ratios in Phases III-V,advanced nitrogen removal was achieved with the effuent total nitrogen being 4.7 mg/L and the nitrogen removal efficiency being 90.5%in Phase *** in-situ and ex-situ activity tests demonstrated the occurrence of partial denitrification and ***,16S rRNA high-throughput sequencing analysis revealed that Candidatus Brocadia was enriched from below the detection limit to in biofilms(0.4%in SBR,2.2%in UASB)and the foc sludge(0.2%in SBR,1.3%in UASB),while Thauera was mainly detected in the foc sludge(8.1%in SBR,8.8%in UASB),which might play a key role in partial ***,this study provides a novel strategy to enrich anammox biomass driven by rapid achievement of partial denitrification through the addition of bio-carriers,which will improve large-scale application of anammox processes in mainstream wastewater treatment.

关键词： Enrichment Anammox biomass Bio-carriers Partial denitrification Mainstream wastewater

Lattice Boltzmann simulation study of anode degradation in solid oxide fuel cells during the initial aging process

在线全文

学校读者我要写书评

暂无评论

International Journal of Minerals,Metallurgy and Materials 2024年第2期31卷 405-411页

作者： Shixue Liu Zhijing Liu Shuxing Zhang Hao Wu Hydrogen Energy Industrial technology Innovation center China Nuclear Power Technology Research InstituteShenzhen 518031China Shenzhen engineering research center for Hydrogen Safety Shenzhen 518031China

For present solid oxide fuel cells(SOFCs),rapid performance degradation is observed in the initial aging process,and the dis-cussion of the degradation mechanism necessitates quantitative ***,focused ion beam-scanning electron microscopy was em-ployed to characterize and reconstruct the ceramic microstructures of SOFC *** lattice Boltzmann method(LBM)simulation of multiphysical and electrochemical processes in the reconstructed models was *** samples collected from industrial-size cells were characterized,including a reduced reference cell and a cell with an initial aging *** parameters of the reconstructed microstructures revealed a significant decrease in the active triple-phase boundary and Ni connectivity in the aged cell compared with the reference *** LBM simulation revealed that activity degradation is dominant compared with microstructural degradation during the initial aging process,and the electrochemical reactions spread to the support layer in the aged *** microstructural and activity de-gradations are attributed to Ni migration and coarsening.

关键词： solid oxide fuel cell anode degradation focused ion beam-scanning electron microscopy lattice Boltzmann method

Removal of rubidium from brine by an integrated film of sulfonated polysulfone/graphene/potassium copper ferricyanide

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Chemical engineering 2024年第5期69卷 112-121页

作者： Huanxi Xu Peihua Lin Pei-Jun Liu Hai-Gang Liu Hui-Bin Guo Chao-Xiang Wu Ming Fang Xu Zhang Guan-Ping Jin Anhui Province engineering research center of Flexible and Intelligent Materials School of Chemistry and Chemical EngineeringHefei University of TechnologyHefei 230009China Chemical Design and research Institute Co. LTD of Qinghai ProvinceQinghai Engineering and Technology Research Center of Fine ChemicalXining 810008China

A novel integrated film of sulfonated polysulfone/graphene/potassium copper ferricyanide(KCuFC/SPSG)was used for selectively extracting rubidium ion(Rb^(+))from *** form KCuFC/SPSG,the precursor film of sulfonated polysulfone/graphene(SPSG)was synthesized by phase conversion process,which was alternately immersed in 0.1 mol·L^(-1)CuSO_(4)/K_(4)[Fe(CN)_(6)]by in-situ adsorption coupled co-precipitation *** data such as nuclear magnetic resonance spectrometer,Fourier transform infrared spectroscope,X-ray photoelectron spectroscope,X-ray diffraction,scanning electron microscope,and energy dispersive spectroscopy all verified that abundant KCuFC were uniformly located on the *** resulting KCuFC/SPSG was used in film separation *** the solution was fed into the system,the Rb^(+)could be selectively adsorption by KCuFC/*** the saturation adsorption,0.5 mol·L^(-1)NH_(4)Cl/HCl was fed into the film cell,Rb^(+)could be quickly desorbed by ion-exchange between Rb^(+)and NH_(4)^(+)in the lattice of *** purpose of separating and recovering Rb^(+)from the brine can be achieved after the repeated *** effects of pH,adsorption time,and interferential ions on the adsorption capacity of Rb^(+)were investigated by batch *** adsorption behavior fits the pseudo-second order kinetic process,while KCuFC has a higher adsorption capacity(Langmuir maximum sorption 165.4 mg·g^(-1)).In addition,KCuFC/SPSG shows excellent selectivity for Rb^(+)even in complex brine ***/SPSG could maintain 93.5%extraction efficiency after five adsorption/desorption cycles.

关键词： Rubidium extraction Potassium copper ferricyanide Sulfonated polysulfone Graphene oxide Adsorption

Facet effects on bimetallic ZnSn hydroxide microcrystals for selective electrochemical CO2 reduction

在线全文

学校读者我要写书评

暂无评论

Green Energy & Environment 2024年第8期9卷 1314-1320页

作者： Liu Han Cheng-wei Wang Shan-shan Luo Ying-tang Zhou Bing Li Ming Liu School of Chemistry and Chemical engineering Harbin Institute of Technology National engineering research center for Marine Aquaculture Marine Science and Technology CollegeZhejiang Ocean University

Employing crystal facets to regulate the catalytic properties in electrocatalytic carbon dioxide reduction reaction（eCO2RR） has been well demonstrated on electrocatalysts containing single metals but rarely explored for bimetallic systems. Here, we synthesize Zn Sn（OH）6（ZSO）microcrystals（MCs） with distinct facets and investigate the facet effects in eCO2RR. Electrochemical studies and in situ Fourier Transform Infrared Spectroscopy（in situ-FTIR） reveal that ZSO MCs produce mainly C1 products of HCOOH and CO. The {111} facet of the ZSO MCS exhibits higher selectivity and faradaic efficiency（FE） than that of the {100} facet over a wide range of potentials（-0.9 V ～-1.3 V versus RHE）. Density Functional Theory（DFT） calculations elucidate that the {111} facet is favorable to the adsorption/activation of CO2molecules,the formation of intermediate in the rate-determining step, and the desorption of C1 products of CO and HCOOH molecules.

关键词： ZnSn(OH) 6 Crystal facets Electrochemical carbon dioxide reduction C1 product Density functional theory

Cooperative composites anchored with single atom Pb and carbon confined PbO nanoparticles for superior lead-carbon batteries

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Journal of Energy Chemistry 2024年第10期97卷 486-497页

作者： Puqiang He Yi Yang Hui Huang Jing Huang Hongbiao Wang Yapeng He Zhongcheng Guo Faculty of Metallurgical and Energy engineering Kunming University of Science and Technology Metallurgical Electrode Material engineering technology research center of Yunnan Province Kunming Hendera technology Co.LTD.

The mitigation of sulphation and parasitic hydrogen evolution is considered as prominent research emphasis for the development of lead-carbon batteries（LCBs） in large-scale energy storage ***,cooperative Pb-C composites consisting of single atom Pb and carbon-encapsulated PbO nanoparticles were prepared by freeze-drying technique and pyrolytic reduction to address above *** innovative use of Pb2+to cross-link sodium alginate enabled a uniform distribution of Pb in the composites,generating Pb-C-PbO three-phase *** analysis and theoretical calculations revealed the synergistic interactions between single-atom Pb and PbO nanoparticles in suppressing parasitic hydrogen evolution and promoting the adsorption of Pb *** presence of monatomic Pb and PbO enhanced the affinity of the composites for the negative active materials and facilitated the transformation of the active materials from bulk into spherical shapes to enhance the specific surface area,thereby counteracting *** the coordinated integration of various functionalities offered by Pb@C-x,the cycle life of the battery at HRPSoC reaches 7025 cycles,which is two times for LCB with pure carbon ***,the discharge capacity increased from 3.52 to 3.79 *** study provides substantial insights into the construction of Pb-C composites for LCBs to inhibit negative sulphation and hydrogen evolution.

关键词： Hydrogen evolution Lead carbon composites Lead-carbon battery Negative sulphation Single-atom