Influence and mechanism of Indonesia vanadium titano-magnetite on metallurgical properties of iron ore sinter

在线全文

学校读者我要写书评

暂无评论

引用

Journal of Central South University 2017年第12期24卷 2805-2812页

作者：高强健魏国沈岩松姜鑫郑海燕沈峰满刘常升 School of Metallurgy Northeastern University Shenyang 110819 China School of Chemical Engineering University of New South Wales Sydney 2052 Australia

In order to provide a reliable reference for utilizing Indonesia vanadium titano-magnetite(VTM) in blast furnace(BF) economically, metallurgical properties of iron ore sinter with addition of Indonesia VTM in mixed sintering materials were investigated, including low-temperature reduction degradation index(RDI), reducibility index(RI), and softening/melting properties. Additionally, influenced mechanism of Indonesia VTM on metallurgical properties of sinter was studied. It is found that adding Indonesia VTM in sintering process quickly increases the RDI of sinters, and decreases the RI from 78.02% to 68.43%. Moreover, both beginning temperature(T_4) and final temperature(TD) of softening/melting increase gradually, and cohesive zone temperature range(T_D–T_4) enlarges from 219 oC to 315 oC. As a result, the permeability of cohesive zone gets worse, which is proven by the higher maximum pressure drop(δPmax) in softening/melting experiments. It is concluded that, after comprehensively considering all metallurgical properties mentioned above, the proper proportion of Indonesia VTM in sintering process is proposed in the new raw materials conditions.

关键词： Indonesia vanadium titano-magnetite sinter reduction degradation index reducibility index softening and melting properties

Thermodynamic studies on gas-based reduction of vanadium titano-magnetite pellets

在线全文

学校读者我要写书评

暂无评论

引用

International Journal of Minerals,Metallurgy and Materials 2019年第7期26卷 822-830页

作者： Jun-wei Chen Yang Jiao Xi-dong Wang Department of Energy and Resources Engineering College of Engineering Peking University

Numerous studies have focused on the reduction thermodynamics of ordinary iron ore;by contrast, the literature contains few thermodynamic studies on the gas-based reduction of vanadium titano-magnetite (VTM) in mixed atmospheres of H2, CO, H2O, CO2, and N2. In this paper, thermodynamic studies on the reduction of oxidized VTM pellets were systematically conducted in an atmosphere of a C–H–O system as a reducing agent. The results indicate that VTM of an equivalent valence state is more difficult to reduce than ordinary iron ore. A reduction equilibrium diagram using the C–H–O system as a reducing agent was obtained;it clearly describes the reduction process. Experiments were performed to investigate the effects of the reduction temperature, the gas composition, and two types of iron ores on the reduction of oxidized VTM pellets. The results show that the final reduction degree increases with increasing reduction temperature, increasing molar ratio of H2/(H2 + CO), and decreasing H2O, CO2, and N2 contents. In addition, the reduction processes under various conditions are discussed. All of the results of the reduction experiments are consistent with those of theoretical thermodynamic analysis. This study is expected to provide valuable thermodynamic theory on the industrial applications of VTM.

关键词： vanadium titano-magnetite gas-based reduction C-H-O system thermodynamics

Influence of microwave treatment on grinding and dissociation characteristics of vanadium titano-magnetite

在线全文

学校读者我要写书评

暂无评论

引用

International Journal of Minerals,Metallurgy and Materials 2019年第2期26卷 160-167页

作者： Jun-peng Wang Tao Jiang Ya-jing Liu Xiang-xin Xue School of Metallurgy Northeastern University Key Laboratory of Liaoning Province for Recycling Science of Metallurgical Resources

The effect of microwave treatment on the grinding and dissociation characteristics of vanadium titano-magnetite(VTM) ore were investigated using scanning electron microscopy(SEM), nitrogen absorption measurements, particle size distribution measurements, X-ray diffraction(XRD) analysis, Fourier transform infrared(FT-IR) spectroscopic analysis, and magnetic separation. SEM analysis showed that microfractures appeared in the microwave-treated VTM, which is attributed to the microwaves' selective heating characteristic and the differential expansion between minerals and gangues. Nitrogen absorption showed that the microfractures were more pronounced when the microwave heating time was increased. Particle size distribution analysis showed that microwave treatment could improve the grindability of the VTM, thus increasing the weight percent of the fine-ground product. The increase in grindability was more significant with prolonged heating time. Moreover, the particle size distribution of the fine-ground product changed only slightly after the microwave treatment. XRD analysis showed that the crystallinity of the microwave-treated VTM increased with increasing microwave heating time. The magnetic separation tests revealed that the separation efficiency increased as a result of the intergranular fractures generated by microwave treatment. The Fe grade of the magnetic fraction of microwave-treated VTM was 1.72% higher than that of the raw ore. We concluded that the microwave treatment was beneficial, especially for the mineral processing characteristics.

关键词： microwave treatment vanadium titano-magnetite grinding microstructure magnetic separation