Ultrasonic testing and microscopic analysis on concrete under sulfate attack and cyclic environment

Journal of Central South University 2014年第12期21卷 4723-4731页

作者：姜磊牛荻涛孙迎召费倩男 College of Civil Engineering Xi’an University of Architecture and Technology

The damage process of concrete exposed to sodium sulfate attack and drying-wetting cycles was investigated. The water to binder(W/B) ratio and the concentration of sulfate solution were taken as variable parameters. Through the experiment, visual change, relative dynamic modulus of elasticity(RDME) and the surface damage layer thickness of concrete were ***, SEM and thermal analysis were used to investigate the changing of microstructure and corrosion products of *** test results show that the ultrasonic velocity is related to the damage layer of concrete. It approves that an increase in damage layer thickness reduces the compactness and the ultrasonic velocity. The deterioration degree of concrete could be estimated effectively by measuring the surface damage layer and the RDME of concrete. It is also found that the content of gypsum in concrete is less than that of ettringite in test, and some gypsum is checked only after a certain corrosion extent. When the concrete is with high W/B ratio or exposed to high concentration of sulfate solution, the content of ettringite first increases and then decreases with corrosion time. However, the content of gypsum increases at a steady rate. The content of corrosion products does not correspond well with the observations of RDME change, and extensive amount of corrosion products can be formed before obvious damage occurs.

关键词： sulfate attack drying-wetting cycles damage layer thickness thermal analysis

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：