Fracture strength of custom-fabricated Celay all-ceramic post and core restored endodontically treated teeth

Chinese Medical Journal 2006年第21期119卷 1815-1820页

作者： ZHANG Yu-xing ZHANG Wei-hong LU Zhi-yue WANG Ke-li Department of Dentistry Beijing Hospital Beijing 100730 China

Background The increased use of all-ceramic crown provides a rationale for tooth-colored core. Due to superior mechanical properties, Vita Celay infiltration ceramic developed for crown and bridge works presents the potential for fabricating all-ceramic posts and cores in one piece. This study was conducted to compare the fracture strength of endodontically treated teeth which were thereafter given different types of posts and cores and crowns restoration, respectively. The evaluated post-and-core systems are： custom-fabricated Celay all-ceramic post-core, custom cast metal post-core, and prefabricated stainless steel post （Parapost） with and without 2.0 mm dentine ferrule. Methods Sixty freshly extracted human maxillary central incisors were endodontically treated and randomly divided into five groups with 12 samples each. Group A： Celay ceramic post-cores restored teeth with 2.0 mm dentine ferrule. Group B： Celay ceramic post-cores restored teeth with no dentine ferrule. Group C： cast metal post-cores restored teeth with 2.0 mm dentine ferrule. Group D： cast metal post-cores restored teeth with no dentine ferrule. Group E： prefabricated post and composite cores restored teeth with 2.0 mm dentine ferrule. All teeth were restored with Celay ceramic crowns. Each specimen was subjected to a load at a 45-degree angle to the long axis on MTS 810 material testing machine until failure, at crosshead speed of 0.02 cm/minute. Analysis of variance followed by the Newman-Keuls pairwise multiple comparison tests were used to compare the results of the groups tested. Results There was a statistically significant difference among the five groups （P〈0.01）. Celay ceramic post-cores restored teeth with 2.0 mm dentine ferrule [（758.35± 119.26） N] and cast metal post-cores restored teeth with 2.0 mm dentine ferrule [（756.63± 166.22） N] had a significantly greater mean fracture strength than the other three groups in which no significant difference was observed. The 2.0 mm dentine fer

关键词： fracture strength ceramics post and core nonvital tooth

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：