Tensile Deformation Behavior of Fe-Mn-Al-C Low Density Steels

Journal of Iron and Steel Research International 2016年第9期23卷 963-972页

作者： Xiao-feng ZHANG Hao YANG De-ping LENG Long ZHANG Zhen-yi HUANG Guang CHEN School of Metallurgical Engineering Anhui University of Technology Ma'anshan 243002 Anhui China School of Materials Science and Engineering Nanjing University of Science and Technology Nanjing 210094 Jiangsu China

Room temperature tensile tests of Fe-Mn-A1 C low density steels with four different chemical compositions were conducted to clarify the dominant deformation mechanisms. Parameters like product of strength and elongation, as well as specific strength and curves of stress-strain relations were calculated. The microstructures and tensile fracture morphologies were observed by optical microscope, scanning electron microscope and transmission electron mi-croscope. The tensile behavior of low density steel was correlated to the microstructural evolution during plastic de formation, and the effects of elements, cooling process and heat treatment temperature on the mechanical properties of the steels were analyzed. The results show that the tensile strength of steels with different cooling modes is more than 1000 MPa. The highest tensile strength of 28Mn-12Al alloy reached 1230 MPa, with corresponding specific strength of 189.16 MPa· cm^3·g^-1 , while the specific strength of 28Mn-10Al alloy was 178.98 MPa·cm^3·g^-1 , and the excellent product of strength and elongation of 28Mn-SAl alloy was over 69.2 GPa·%. A large number of ferrite reduced the ductility and strain hardening rate of the alloy, while the existence of κ carbides may improve the strength but weaken the plasticity. Some fine κ carbides appeared in the water-quenched specimen, while coarse carbides were observed in the air-cooled specimen. High temperature heat treatment improved the decomposition ki- netics of 7 phase and the diffusion rate of carbon, thus speeded up the precipitation of fine κ carbides. The dominant deformation mechanism of low density steel was planar glide, including shear-band-induced plasticity and microband- induced plasticity.

关键词： low density steel carbide deformation mechanism planar glide shear band-induced plasticity microband-induced plasticity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：