IMPROVING THE SURFACE PROPERTY OF TC4 ALLOY BY laser NITRIDING AND ITS MECHANISM

Acta Metallurgica Sinica(English Letters) 2006年第2期19卷 151-156页

作者： Y.L. Yang G.J. Zhao D. Zhang C.S. Liu Gollege of Sdence Northeastern University Shenyang 110004 Ghina College of Material and Metallurgy Northeastern University Shenya g 110004 China

The mixing technology of laser and heated nitrogen was applied to improve the surface hardness of titanium alloy （ TC4 ）. The samples were nitrided with laser power density of 6.S × 10^6SW. cm^-2, the scanning speed varioas from 100 to 500mm ·min^-1. The nitrogen gas was pre-heated to 300℃ to accelerate the nitriding process. Some interested samples were tested with XRD method （X-ray diffraction） to analyze the composition of nitrides, and the surface hardness of HV was measured. The results show that TiN and Ti2N were formed on the surface of Ti alloy with proper nitriding parameters, but TiN is the main composition. The surface hardness increased by three times, which is from the original value of 269to 794kg·mm^-2. The mechanism of the mixing technology is considered mainly of the activation of nitrogen by laser power and the pre-heated process which accelerated the nitriding process. The nitridation process can be considered as six steps given in detail. The result by analyzing the mechanism of improving the surface property of TiAl alloy shows the improvement of surface property due to two factors： the first reason is the result of laser annealing, and the second one is the formation of TiN.

关键词： laser nitridation surface property Ti alloy

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：