Nano Cr Interlayered CrN Coatings on Steels

Tsinghua Science and Technology 2005年第6期10卷 690-698页

作者： Pranav Deshpande Department of Chemical and Materials Engineering M.L. #12 University of Cincinnati Cincinnati OH 45242 USA

CrN coated steels assisted with a nano Cr interlayer were investigated. The Cr nano-interlayers were prepared by sputter deposition with a thickness about 70-100 nm. CrN coatings were also prepared by sputter deposition on the Cr nano-interlayers. The crystal structures, microhardness, and scratch resistance of CrN/Cr coatings were determined. Results show that the Cr nano-interlayers improve scratch resistance and the microhardness of CrN coated steels. A rapid heat treatment with infrared （IR） was performed for coated specimens in the attempt to improve bonding, With IR heat treatments, the beneficial effect of the Cr nano-interlayers was clearly observed. Without the Cr nano-interlayers, severe cracks on the surface of coatings were observed after IR heat treatment. However, with a Cr interlayer, no cracks on the surface of CrN coatings were observed after the heat treatment. The scratch resistance of coatings was also affected by the Cr nano-interlayers. The scratch track was clean and showed significantly smaller amount of scratch debris for CrN coatings with Cr interlayers than those without the Cr nano-interlayers. The microhardness of coatings with the Cr nano-interlayers is higher than those without the Cr nano-interlayers after IR heat treatment. The Cr and CrN phase have been identified with X-ray diffraction analysis, and the results show that the higher the nitrogen content in the sputtering gas, the stronger the CrN peaks observed in the diffraction patterns are.

关键词： hard chromium replacement chromium nitride chromium nano-interlayer reactive sputter deposition infrared heat treatment

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：