HAZ CRACKING AND hot ductility OF Ni_3AI CONTAINING Zr ALLOY

Acta Metallurgica Sinica(English Letters) 2000年第1期13卷 94-97页

作者： B. N. Qian J. L. Li J. T. Guo and B. Z. Wei (1)Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110015, China 2)Shanghai University, Shanghai 200072, China)

The HAZ cracking test in EB welding condition and hot ductility test show that the cracking mechanism is the formation of Ni - Ni5Zr eutectic which is resulting from the enrichment of Zr in grain boundaries during *** order to eliminate HAZ cracks the diffusion and recrystalization anealing treatment after cast and during cold rolling should be conducted in vacuum or protecting atmosphere and at the same time a slow welding speed is necessary.

关键词： Ni_3Al bearing Zr alloy liquation cracking hot ductility test

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：